| Aplikasi | Kain dan serat non-anyaman |
Barang | Kualitas Indeks | Hasil tes | Metode pengujian | |
| Modulus Lentur (MPA) | ≥1000 | 1208 | GB/T9341 | |
Penampilan hitam (pcs/kg) | 0 | 0 | Sh/t1541.i | |
Penampilan Black Spots (PCS/KG) | <5 | 0 | Sh/t1541.i | |
Penampilan besar dan kecil (g/kg) | <10 | 3.8931 | SH/T 1541.1 | |
Kotoran penampilan (PCS/kg) | 0 | 0 | SH/T 1541.1 | |
| Indeks isotaktik (fraksi massa%) | ≥96.5 | 96.8 | GB/T2412 | |
| Mata Ikan 0.8mm (PCS/1520cm^2) | ≤5 | 1 | GB/T6595 | |
| Mata Ikan 0.4mm (PCS/1520cm^2) | ≤15 | 1 | GB/T6595 | |
| Indeks Kuning | ≤0 | -0.6 | HG/T3862 | |
| Kandungan abu granular (%fraksi massa) | ≤0.0250 | 0.0158 | GB/T9345.I | |
| Laju aliran massa meleleh (G/10 menit) | 40.5-49.5 | 43.6 | GB/T3682.1 | |
| Sifat Tarik Modulus Elastis Tarik (ET) (MPA) | ≥1100 | 1239 | GB/T1040.2 | |
| Sifat tarik stres hasil tarik (OY) (MPA) | ≥30.0 | 30.4 | GB/T1040.2 | |
| Sifat Tarik Tarik Stres Pemecah Tarik (B) (MPA) | ≥13.0 | 17.6 | GB/T1040.2 | |
| Properti Tarik Nominal Breaking Tensile | ≥300 | 541 | GB/T1040.2 | |
|
|
|
 |  |  |
| Aplikasi | Kain dan serat non-anyaman |
Barang | Kualitas Indeks | Hasil tes | Metode pengujian | |
| Modulus Lentur (MPA) | ≥1000 | 1208 | GB/T9341 | |
Penampilan hitam (pcs/kg) | 0 | 0 | Sh/t1541.i | |
Penampilan Black Spots (PCS/KG) | <5 | 0 | Sh/t1541.i | |
Penampilan besar dan kecil (g/kg) | <10 | 3.8931 | SH/T 1541.1 | |
Kotoran penampilan (PCS/kg) | 0 | 0 | SH/T 1541.1 | |
| Indeks isotaktik (fraksi massa%) | ≥96.5 | 96.8 | GB/T2412 | |
| Mata Ikan 0.8mm (PCS/1520cm^2) | ≤5 | 1 | GB/T6595 | |
| Mata Ikan 0.4mm (PCS/1520cm^2) | ≤15 | 1 | GB/T6595 | |
| Indeks Kuning | ≤0 | -0.6 | HG/T3862 | |
| Kandungan abu granular (%fraksi massa) | ≤0.0250 | 0.0158 | GB/T9345.I | |
| Laju aliran massa meleleh (G/10 menit) | 40.5-49.5 | 43.6 | GB/T3682.1 | |
| Sifat Tarik Modulus Elastis Tarik (ET) (MPA) | ≥1100 | 1239 | GB/T1040.2 | |
| Sifat tarik stres hasil tarik (OY) (MPA) | ≥30.0 | 30.4 | GB/T1040.2 | |
| Sifat Tarik Tarik Stres Pemecah Tarik (B) (MPA) | ≥13.0 | 17.6 | GB/T1040.2 | |
| Properti Tarik Nominal Breaking Tensile | ≥300 | 541 | GB/T1040.2 | |
|
|
|
| | |