Features | high flow |
Application | automotive applications, automotive external parts, automotive internal parts |
Analysis Item | Quality Index | Test result | Experiment method |
Granular Appearance, Color granules.pc/kg | ≤8 | 2 | SH/T1541-2006 |
Melt mass flow rate, g/10min | 8~11 | 9.51 | GB/T3682.1-2018 |
Tensile stress at break, MPa | ≥17 | 19.7 | GB/T9341-2008 |
Flexural modulus,MPa | ≥900 | 1030 | GB/T9341-2008 |
Charpy impact strength (A-type notch), GB/T9341-2008 KJ/m^2 | ≥40 | 52.3 | GB/T1043.1-2008 |
Yellow index | ≤0 | -2 | GB/T 3862-2006 |
![]() | ![]() | ![]() |
Features | high flow |
Application | automotive applications, automotive external parts, automotive internal parts |
Analysis Item | Quality Index | Test result | Experiment method |
Granular Appearance, Color granules.pc/kg | ≤8 | 2 | SH/T1541-2006 |
Melt mass flow rate, g/10min | 8~11 | 9.51 | GB/T3682.1-2018 |
Tensile stress at break, MPa | ≥17 | 19.7 | GB/T9341-2008 |
Flexural modulus,MPa | ≥900 | 1030 | GB/T9341-2008 |
Charpy impact strength (A-type notch), GB/T9341-2008 KJ/m^2 | ≥40 | 52.3 | GB/T1043.1-2008 |
Yellow index | ≤0 | -2 | GB/T 3862-2006 |
![]() | ![]() | ![]() |