Features | high strength |
Application | automotive applications, small household appliances |
Analysis Item | Quality Index | Test result | Experiment method |
Yellow index | ≤2.0 | -1.9 | HG/T3862 |
Color granule , pcs/kg | ≤6 | 2 | SH/T 1541.1 |
Melt mass flow rate, g/10min | 28.0-33.0 | 29.6 | GB/T3682.1-2018,230C/2.16kg |
Tensile fracture stress,Mpa | ≥22.0 | 24.2 | GB/T1040.2 |
Flexural modulus, MPa | ≥1100 | 1374 | GB/T 9341 |
Charpy notched impact strength (23) , kJ/m^3 | ≥8.0 | 9.7 | GB/T 1043.1 |
![]() | ![]() | ![]() |