| Features | High impact resistance |
| Application | Household daily necessities, food packaging, packaging |
Analysis Item | Quality Index | Test Results | Experiment method |
Particle appearance (colorparticles),pcs/kg | ≤40 | 0 | SH/T 1541-2006 |
Melt massflow rate (5kg),g/10min | 3.9-5.7 | 4.5 | GB/T 3682-2000 |
Tensile yield stress MPa | Measured | 26.4 | GB/T 1040.2-2006 |
Vicat softening point,℃ | ≥80 | 88.9 | GB/T 1633-2000 |
Charpy impact strength, kJ/m^2 | ≥7.0 | 11 | GB/T 1043.1-2008 |
Yellow Index (Z-Y) | 9-19 | 9.4 | ASTM E313 |
Residualstyrene monomer,10^-6(wt) | ≤600 | 298 | GB/T 16867-1997 |
|
|  |
 |  |  |
| Features | High impact resistance |
| Application | Household daily necessities, food packaging, packaging |
Analysis Item | Quality Index | Test Results | Experiment method |
Particle appearance (colorparticles),pcs/kg | ≤40 | 0 | SH/T 1541-2006 |
Melt massflow rate (5kg),g/10min | 3.9-5.7 | 4.5 | GB/T 3682-2000 |
Tensile yield stress MPa | Measured | 26.4 | GB/T 1040.2-2006 |
Vicat softening point,℃ | ≥80 | 88.9 | GB/T 1633-2000 |
Charpy impact strength, kJ/m^2 | ≥7.0 | 11 | GB/T 1043.1-2008 |
Yellow Index (Z-Y) | 9-19 | 9.4 | ASTM E313 |
Residualstyrene monomer,10^-6(wt) | ≤600 | 298 | GB/T 16867-1997 |
|
| |
| | |