Application | mainly used in food packaging, thermoformed plate products, selling cups, lateral extrusion, medical packaging, hard packaging, refrigerator parts, flame retardant additives, electrical and electronic internals |
Analysis Item | Quality Index | Test Results | Experiment method |
Particle appearance (colorparticles),pcs/kg | ≤40 | 0 | SH/T 1541-2006 |
Melt massflow rate (5.00kg), g/10min | 2.0-4.0 | 3.03 | ISO 1133:2005 |
Tensilestrength, MPa | Measured | 29.6 | ISO 527-2:1993 |
Vicat softening point, ℃ | ≥84 | 91.2 | ISO 306:2004 |
Charpy impact strength, kJ/mü | ≥8.0 | 11 | ISO 179-1 |
Yellow Index (Z-Y) | 9-19 | 9.7 | ASTM E-308-1 |
Residualstyrene monomer, 10^-6(wt) | <600 | 295 | GB/T 16867-1997 |
![]() | ![]() | ![]() |
Application | mainly used in food packaging, thermoformed plate products, selling cups, lateral extrusion, medical packaging, hard packaging, refrigerator parts, flame retardant additives, electrical and electronic internals |
Analysis Item | Quality Index | Test Results | Experiment method |
Particle appearance (colorparticles),pcs/kg | ≤40 | 0 | SH/T 1541-2006 |
Melt massflow rate (5.00kg), g/10min | 2.0-4.0 | 3.03 | ISO 1133:2005 |
Tensilestrength, MPa | Measured | 29.6 | ISO 527-2:1993 |
Vicat softening point, ℃ | ≥84 | 91.2 | ISO 306:2004 |
Charpy impact strength, kJ/mü | ≥8.0 | 11 | ISO 179-1 |
Yellow Index (Z-Y) | 9-19 | 9.7 | ASTM E-308-1 |
Residualstyrene monomer, 10^-6(wt) | <600 | 295 | GB/T 16867-1997 |
![]() | ![]() | ![]() |