Features | high impact resistance, high strength and transparency |
Application | plastic bag |
Analysis Item | Quality Index | Test result | Experiment method |
Dark spots and Color granule, pcs/kg | ≤6 | 4 | SH/T1541.1 |
Snake skin and tail granule, pcs/kg | ≤15 | 9 | SH/T1541.1 |
Melt mass flow rate, g/10min | 7.00~13.0 | 9.62 | GB/T3682.1-2018 |
Tensile stress at break, MPa | ≥21 | 23.5 | GB/T1040.2 |
Tensile Strength Tensile Strain,% | ≥600 | 704 | GB/T1040.2 |
Fisheye 0.4mm, each/1520cm^3 | ≤20 | 6 | GB/T11115-2009 |
Fisheye 0.8mm, each/1520cm^3 | ≤8 | 1 | GB/T11115-2009 |
Density, g/cm^3 | 0.9220~0.9260 | 0.9245 | GB/T 1033.2 |
Large and small granules | ≤5 | 1 | SH/T 1541.1 |
Haze degree (film thickness 0.030mm) % | ≤10 | 6 | GB/T 2410 |
Openness | Easy to open | Easy to open | - |
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Features | high impact resistance, high strength and transparency |
Application | plastic bag |
Analysis Item | Quality Index | Test result | Experiment method |
Dark spots and Color granule, pcs/kg | ≤6 | 4 | SH/T1541.1 |
Snake skin and tail granule, pcs/kg | ≤15 | 9 | SH/T1541.1 |
Melt mass flow rate, g/10min | 7.00~13.0 | 9.62 | GB/T3682.1-2018 |
Tensile stress at break, MPa | ≥21 | 23.5 | GB/T1040.2 |
Tensile Strength Tensile Strain,% | ≥600 | 704 | GB/T1040.2 |
Fisheye 0.4mm, each/1520cm^3 | ≤20 | 6 | GB/T11115-2009 |
Fisheye 0.8mm, each/1520cm^3 | ≤8 | 1 | GB/T11115-2009 |
Density, g/cm^3 | 0.9220~0.9260 | 0.9245 | GB/T 1033.2 |
Large and small granules | ≤5 | 1 | SH/T 1541.1 |
Haze degree (film thickness 0.030mm) % | ≤10 | 6 | GB/T 2410 |
Openness | Easy to open | Easy to open | - |
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |