| Features | High strength, stress cracking resistance |
| Application | food, hospital supplies, profiles |
Function | Method | Unit | Value |
| ISO 1133-1 | g/10min | 0.35 | |
| Density (23°C) | ISO 1183-2 | g/cm^3 | 0.956 |
| Tensile yield strength | ISO 527-2 | MPa | 27 |
| Yield elongation | ISO 527-2 | % | 9 |
| Tensile breaking strength | ISO 527-2 | MPa | 10 |
| Elongation at break | ISO 527-2 | % | 530 |
| Elastic Modulus | ISO 527-2 | MPa | 1190 |
| Flexural modulus | ISO 178 | MPa | 1310 |
| IZOD notched impact strength (23°C) | ISO 180 | kJ/m^2 | 11 |
| Melting point | ISO 11357-3 | ℃ | 134 |
| Vicat softening temperature, A/50 | ISO 306 | ℃ | 129 |
| Environmental stress cracking resistance, F50 | ASTM D1693 | Hours | 14 |
 |  |
 |  |  |
| Features | High strength, stress cracking resistance |
| Application | food, hospital supplies, profiles |
Function | Method | Unit | Value |
| ISO 1133-1 | g/10min | 0.35 | |
| Density (23°C) | ISO 1183-2 | g/cm^3 | 0.956 |
| Tensile yield strength | ISO 527-2 | MPa | 27 |
| Yield elongation | ISO 527-2 | % | 9 |
| Tensile breaking strength | ISO 527-2 | MPa | 10 |
| Elongation at break | ISO 527-2 | % | 530 |
| Elastic Modulus | ISO 527-2 | MPa | 1190 |
| Flexural modulus | ISO 178 | MPa | 1310 |
| IZOD notched impact strength (23°C) | ISO 180 | kJ/m^2 | 11 |
| Melting point | ISO 11357-3 | ℃ | 134 |
| Vicat softening temperature, A/50 | ISO 306 | ℃ | 129 |
| Environmental stress cracking resistance, F50 | ASTM D1693 | Hours | 14 |
| |
| | |