| Quantitas: | |
|---|---|
| Features | Princeps vires, accentus cracking resistentia |
| Applicatio | Cibus hospitium commeatus profiles |
Munus | Ratio | Unitas | Valor |
| ISO 1133-1 | G / 10min | 0.35 | |
| Density (XXIII ° F) | ISO 1183-2 | G / III cm ^ | 0.956 |
| Tensile cede vires | ISO 527-2 | MPA | 27 |
| Cedere elongatio | ISO 527-2 | % | 9 |
| Tensile solveret vires | ISO 527-2 | MPA | 10 |
| Elongatio ad confractus | ISO 527-2 | % | 530 |
| Elastica modulus | ISO 527-2 | MPA | 1190 |
| Flexural modulum | ISO CLXXVIII | MPA | 1310 |
| Izod nowched impulsum vires (XXIII ° F) | ISO CLXXX | KJ / m ^ II | 11 |
| Point liquescens | ISO 11357-3 | ℃ | 134 |
| Vicat mollitorum temperatus a / L | ISO CCCVI | ℃ | 129 |
| Environmental accentus fregisset resistentia, F50 | ASTM D1693 | Horulus | 14 |
 |  |
 |  |  |
| Features | Princeps vires, accentus cracking resistentia |
| Applicatio | Cibus hospitium commeatus profiles |
Munus | Ratio | Unitas | Valor |
| ISO 1133-1 | G / 10min | 0.35 | |
| Density (XXIII ° F) | ISO 1183-2 | G / III cm ^ | 0.956 |
| Tensile cede vires | ISO 527-2 | MPA | 27 |
| Cedere elongatio | ISO 527-2 | % | 9 |
| Tensile solveret vires | ISO 527-2 | MPA | 10 |
| Elongatio ad confractus | ISO 527-2 | % | 530 |
| Elastica modulus | ISO 527-2 | MPA | 1190 |
| Flexural modulum | ISO CLXXVIII | MPA | 1310 |
| Izod nowched impulsum vires (XXIII ° F) | ISO CLXXX | KJ / m ^ II | 11 |
| Point liquescens | ISO 11357-3 | ℃ | 134 |
| Vicat mollitorum temperatus a / L | ISO CCCVI | ℃ | 129 |
| Environmental accentus fregisset resistentia, F50 | ASTM d1693 | Horulus | 14 |
| |
| | |