| Applicatio | Containers, plastic utres |
Project |
Unitas |
Index Technical |
Results |
Experimentum modum |
|
CALLA |
Nigrum Spotand Colo colui cultum grana |
PC / kg |
≤6 |
2 |
SH / T 1541,1 |
Missam fluxus rate |
CXC ℃, 21.6kg |
G / 10min |
XXVIII ~ XXXVIII |
31.6 |
GB / T 3682,1 |
Densitas |
G / CM3 |
0.951 ~ ~ 0.955 |
0.9545 |
GB / T 1033,2 |
|
Tensile cede accentus |
MPA |
≥23 |
26.6 |
GB / T 1040.2 |
|
Tensal nominis ametat confractus |
% |
≥150 |
211 |
||
Prandium robustus Roged Impact |
KJ / m ^ II |
≥7 |
10 |
GB / T 1043,1 |
|
Flexural modulum |
MPA |
≥700 |
1120 |
GB / T (IX) CCCXLI |
|
 |
 |
 |
 |
 |
| Applicatio | Containers, plastic utres |
Project |
Unitas |
Index Technical |
Results |
Experimentum modum |
|
CALLA |
Nigrum Spotand Colo colui cultum grana |
PC / kg |
≤6 |
2 |
SH / T 1541,1 |
Missam fluxus rate |
CXC ℃, 21.6kg |
G / 10min |
XXVIII ~ XXXVIII |
31.6 |
GB / T 3682,1 |
Densitas |
G / CM3 |
0.951 ~ ~ 0.955 |
0.9545 |
GB / T 1033,2 |
|
Tensile cede accentus |
MPA |
≥23 |
26.6 |
GB / T 1040.2 |
|
Tensal nominis ametat confractus |
% |
≥150 |
211 |
||
Prandium robustus Roged Impact |
KJ / m ^ II |
≥7 |
10 |
GB / T 1043,1 |
|
Flexural modulum |
MPA |
≥700 |
1120 |
GB / T (IX) CCCXLI |
|
|
|
|
|
|