| Features | Minimum temperatus resistentia, princeps rigiditatem |
| Applicatio | familia necessitatibus, vasis, cibum packaging |
Analysis Item | Index | TRIEN | Experimentum modum |
| Analysis Project | Index | TRIEN | Experimentum modum |
Specie particulae Color particulas, PCs / kg magna et parva grana, g / kg | ≤ X ≤ X | 0 0 | Sh / T 1541-2006 |
| Missam fluxus rate (2.16kg), G / 10min | 0,25 ± 0.06 | 0.25 | Q / sq ds DVII |
| Density, kg / m ā | CMLIII ± 2.5 | 954.2 | ISO 1183-2 |
| Tensile cede accentus, MPA | ≥21.0 | 25.5 | Q / sq ds DI |
| Tensile fractura accentus, MPa | ≥ 15.0 | 31.3 | Q / sq ds DI |
| Tensile iactabantur ad confractus,% | ≥500 | 1197 | Q / sq ds DI |
| Flexural modulum, MPA | ≥800 | 1248 | Q / sq ds MMII |
 |  |
 |  |  |
| Features | Minimum temperatus resistentia, princeps rigiditatem |
| Applicatio | familia necessitatibus, vasis, cibum packaging |
Analysis Item | Index | TRIEN | Experimentum modum |
| Analysis Project | Index | TRIEN | Experimentum modum |
Specie particulae Color particulas, PCs / kg magna et parva grana, g / kg | ≤ X ≤ X | 0 0 | Sh / T 1541-2006 |
| Missam fluxus rate (2.16kg), G / 10min | 0,25 ± 0.06 | 0.25 | Q / sq ds DVII |
| Density, kg / m ā | CMLIII ± 2.5 | 954.2 | ISO 1183-2 |
| Tensile cede accentus, MPA | ≥21.0 | 25.5 | Q / sq ds DI |
| Tensile fractura accentus, MPa | ≥ 15.0 | 31.3 | Q / sq ds DI |
| Tensile iactabantur ad confractus,% | ≥500 | 1197 | Q / sq ds DI |
| Flexural modulum, MPA | ≥800 | 1248 | Q / sq ds MMII |
| |
| | |