Features | low temperature resistance, high rigidity |
Application | household necessities, containers, food packaging |
Analysis Item | Quality Index | Test result | Experiment method |
Analysis Project | Quality Index | Test result | Experiment method |
Particle appearance Color particles, pcs/kg Large and small grains, g/kg | ≤ 10 ≤ 10 | 0 0 | SH/T 1541-2006 |
Melt mass flow rate (2.16kg), g/10min | 0.25±0.06 | 0.25 | Q/SY DS 0507 |
Density, kg/m ā | 953±2.5 | 954.2 | ISO 1183-2 |
Tensile yield stress, MPa | ≥21.0 | 25.5 | Q/SY DS 0501 |
Tensile fracture stress, MPa | ≥ 15.0 | 31.3 | Q/SY DS 0501 |
Tensile strain at break,% | ≥500 | 1197 | Q/SY DS 0501 |
Flexural modulus, MPa | ≥800 | 1248 | Q/SY DS 0502 |
![]() | ![]() |
![]() | ![]() | ![]() |
Features | low temperature resistance, high rigidity |
Application | household necessities, containers, food packaging |
Analysis Item | Quality Index | Test result | Experiment method |
Analysis Project | Quality Index | Test result | Experiment method |
Particle appearance Color particles, pcs/kg Large and small grains, g/kg | ≤ 10 ≤ 10 | 0 0 | SH/T 1541-2006 |
Melt mass flow rate (2.16kg), g/10min | 0.25±0.06 | 0.25 | Q/SY DS 0507 |
Density, kg/m ā | 953±2.5 | 954.2 | ISO 1183-2 |
Tensile yield stress, MPa | ≥21.0 | 25.5 | Q/SY DS 0501 |
Tensile fracture stress, MPa | ≥ 15.0 | 31.3 | Q/SY DS 0501 |
Tensile strain at break,% | ≥500 | 1197 | Q/SY DS 0501 |
Flexural modulus, MPa | ≥800 | 1248 | Q/SY DS 0502 |
![]() | ![]() |
![]() | ![]() | ![]() |