| Features | easy processing, high rigidity, stress cracking resistance and chemical resistance |
| Application | container |
Analysis Item | Quality Index | Test result | Experiment method |
Granular appearance Color particles, pcs/kg Large and small grains, g/kg | ≤ 40 ≤ 10 | 0 0 | SH/T 1541-2006 |
| Melt mass flow rate (2.16kg), g/10min | 1.5～2.5 | 1.9 | GB/T 3682-2000 |
| Density g/cm^3 | 0.947～0.954 | 0.9506 | GB/T 1033.2-2010 |
| Charpy impactstrength kJ/mü | ≥40 | 56 | GB/T 1043.1-2008 |
| Tensileyieldstress MPa | ≥ 22.0 | 25.6 | GB/T 1040.2-2006 |
| Nominalstrain atbreak in % | ≥350 | 836 | GB/T 1040.2-2006 |
| Flexural modulus MPa | ≥900 | 1234 | GB/T 9341-2008 |
 |  |  |  |
 |  |  |
| Features | easy processing, high rigidity, stress cracking resistance and chemical resistance |
| Application | container |
Analysis Item | Quality Index | Test result | Experiment method |
Granular appearance Color particles, pcs/kg Large and small grains, g/kg | ≤ 40 ≤ 10 | 0 0 | SH/T 1541-2006 |
| Melt mass flow rate (2.16kg), g/10min | 1.5～2.5 | 1.9 | GB/T 3682-2000 |
| Density g/cm^3 | 0.947～0.954 | 0.9506 | GB/T 1033.2-2010 |
| Charpy impactstrength kJ/mü | ≥40 | 56 | GB/T 1043.1-2008 |
| Tensileyieldstress MPa | ≥ 22.0 | 25.6 | GB/T 1040.2-2006 |
| Nominalstrain atbreak in % | ≥350 | 836 | GB/T 1040.2-2006 |
| Flexural modulus MPa | ≥900 | 1234 | GB/T 9341-2008 |
| | | |
| | |