| Cainníocht: | |
|---|---|
| Bheith | Neart ard, friotaíocht scoilteadh struis |
| Iarrchán | bia, soláthairtí ospidéil, próifílí |
Feidhmigh |
Modh |
Aonad |
Luach |
| ISO 1133-1 | g/10min |
0.35 | |
| Dlús (23 ° C) | ISO 1183-2 | g/cm^3 | 0.956 |
| Neart toraidh teanntachta | ISO 527-2 | MPA | 27 |
| Fadú táirgeachta | ISO 527-2 | % | 9 |
| Neart briste teanntachta | ISO 527-2 | MPA | 10 |
| Fadú ag sos | ISO 527-2 | % | 530 |
| Modulus leaisteach | ISO 527-2 | MPA | 1190 |
| Modal Flexural | ISO 178 | MPA | 1310 |
| Neart tionchair izod notched (23 ° C) | ISO 180 | kj/m^2 | 11 |
| Leáphointe | ISO 11357-3 | ℃ | 134 |
| Teocht softening vicat, a/50 | ISO 306 | ℃ | 129 |
| Friotaíocht Scáineadh Strus Comhshaoil, F50 | ASTM D1693 | Uair | 14 |
 |
 |
 |
 |
 |
| Bheith | Neart ard, friotaíocht scoilteadh struis |
| Iarrchán | bia, soláthairtí ospidéil, próifílí |
Feidhmigh |
Modh |
Aonad |
Luach |
| ISO 1133-1 | g/10min |
0.35 | |
| Dlús (23 ° C) | ISO 1183-2 | g/cm^3 | 0.956 |
| Neart toraidh teanntachta | ISO 527-2 | MPA | 27 |
| Fadú táirgeachta | ISO 527-2 | % | 9 |
| Neart briste teanntachta | ISO 527-2 | MPA | 10 |
| Fadú ag sos | ISO 527-2 | % | 530 |
| Modulus leaisteach | ISO 527-2 | MPA | 1190 |
| Modal Flexural | ISO 178 | MPA | 1310 |
| Neart tionchair izod notched (23 ° C) | ISO 180 | kj/m^2 | 11 |
| Leáphointe | ISO 11357-3 | ℃ | 134 |
| Teocht softening vicat, a/50 | ISO 306 | ℃ | 129 |
| Friotaíocht Scáineadh Strus Comhshaoil, F50 | ASTM D1693 | Uair | 14 |
|
|
|
|
|