| Features | high strength |
| Application | wire drawing |
Analysis Item | Quality Index | Test result | Experiment method |
| Project | Quality Index | Test result | Experiment method |
| Color particles, pcs/kg | ≤5 | 0 | SH/T 1541 |
| Black grains, pcs/kg | ≤0 | 0 | SH/T 1541 |
| Size grain, g/kg | Measured | 1 | SH/T 1541 |
| Melt mass flow rate (MFR), g/10min | 2.7-4 | 3.52 | GB/T 3682.1 |
| Bending modulus,Mpa | ≥1500 | 1973 | GB/T 2412 |
| Ash (mass fraction), mg/kg | ≤500 | 381 | GB/T 9345.1 |
| Tensile yield stress ( σy), MPa | Measured | 41 | GB/T 1040.2 |
| Vica softening point,℃ | ≥154 | 162.3 | GB/T 1633 |
| Haze, % | ≤6 | 1.5 | GB/T 2410 |
| The chloride content of ,mg/kg | ≤40 | 26 | Q/SY JX0324 |
| Fisheye (0.4mm), pcs/1520cm^2 | ≤15 | 9 | GB/T 6595 |
 |  |  |  |
 |  |  |
| Features | high strength |
| Application | wire drawing |
Analysis Item | Quality Index | Test result | Experiment method |
| Project | Quality Index | Test result | Experiment method |
| Color particles, pcs/kg | ≤5 | 0 | SH/T 1541 |
| Black grains, pcs/kg | ≤0 | 0 | SH/T 1541 |
| Size grain, g/kg | Measured | 1 | SH/T 1541 |
| Melt mass flow rate (MFR), g/10min | 2.7-4 | 3.52 | GB/T 3682.1 |
| Bending modulus,Mpa | ≥1500 | 1973 | GB/T 2412 |
| Ash (mass fraction), mg/kg | ≤500 | 381 | GB/T 9345.1 |
| Tensile yield stress ( σy), MPa | Measured | 41 | GB/T 1040.2 |
| Vica softening point,℃ | ≥154 | 162.3 | GB/T 1633 |
| Haze, % | ≤6 | 1.5 | GB/T 2410 |
| The chloride content of ,mg/kg | ≤40 | 26 | Q/SY JX0324 |
| Fisheye (0.4mm), pcs/1520cm^2 | ≤15 | 9 | GB/T 6595 |
| | | |
| | |