| Pe100 | X MPA |
| Applicatio | Pe tubo, Gas pipe |
Analysis Item |
Index |
TRIEN |
Test modus |
Meltare massflowrate (5kg), G / 10min |
0,30 ± 0.06 |
0.31 |
Q / sq ds DVII |
Density, kg / mā |
CMLX ± II |
959.7 |
ISO 1183-2 |
TensileyieldStress, MPA |
≥21.0 |
22.2 |
Q / sq ds DI |
Tensilestrain atbreak,% |
≥350 |
770 |
Q / sq ds DI |
Principium impacttrength, KJ / m ^ II |
≥22.0 |
27.2 |
Q / Sy DS D3 |
Carbon Nigrum Dispersion, Smartclass |
≤3 |
2.3 |
Q / sq ds DVIII |
Oxidatio inductione tempore (Isothermal oit) (CCX ℃), min |
≥20 |
60.7 |
GB / T 19466.6-2009 |
Carbon Nigrum contentus, M / M% |
2.0-2.5 |
2.17 |
GB 13021-1991 |
Humorem,% |
Meteptor |
0.006 |
Sh / T 1770-2010 |
 |
 |
 |
 |
 |
 |
 |
| Pe100 | X MPA |
| Applicatio | Pe tubo, Gas pipe |
Analysis Item |
Index |
TRIEN |
Test modus |
Meltare massflowrate (5kg), G / 10min |
0,30 ± 0.06 |
0.31 |
Q / sq ds DVII |
Density, kg / mā |
CMLX ± II |
959.7 |
ISO 1183-2 |
TensileyieldStress, MPA |
≥21.0 |
22.2 |
Q / sq ds DI |
Tensilestrain atbreak,% |
≥350 |
770 |
Q / sq ds DI |
Principium impacttrength, KJ / m ^ II |
≥22.0 |
27.2 |
Q / Sy DS D3 |
Carbon Nigrum Dispersion, Smartclass |
≤3 |
2.3 |
Q / sq ds DVIII |
Oxidatio inductione tempore (Isothermal oit) (CCX ℃), min |
≥20 |
60.7 |
GB / T 19466.6-2009 |
Carbon Nigrum contentus, M / M% |
2.0-2.5 |
2.17 |
GB 13021-1991 |
Humorem,% |
Meteptor |
0.006 |
Sh / T 1770-2010 |
|
|
|
|
|
|
|