| PE100 | 10 MPa |
| Permohonan | Tiub PE, paip gas |
Item analisis | Indeks Kualiti | Hasil ujian | Kaedah ujian |
Melt Massflowrate (5kg), G/10min | 0.30 ± 0.06 | 0.31 | Q/SY DS 0507 |
Ketumpatan, kg/mā | 960 ± 2 | 959.7 | ISO 1183-2 |
Tensileyieldstress, MPA | ≥21.0 | 22.2 | Q/SY DS 0501 |
Tensilestrain atbreak, % | ≥350 | 770 | Q/SY DS 0501 |
Charpy ImpactStrength, kJ/m^2 | ≥22.0 | 27.2 | Q/SY DS 0503 |
Penyebaran hitam karbon, sizeclass | ≤3 | 2.3 | Q/SY DS 0508 |
Masa induksi pengoksidaan (isothermal OIT) (210 ℃), min | ≥20 | 60.7 | GB/T 19466.6-2009 |
Kandungan Hitam Karbon, M/M% | 2.0-2.5 | 2.17 | GB 13021-1991 |
Kelembapan, % | Diukur | 0.006 | SH/T 1770-2010 |
 |  |  |  |
 |  |  |
| PE100 | 10 MPa |
| Permohonan | Tiub PE, paip gas |
Item analisis | Indeks Kualiti | Hasil ujian | Kaedah ujian |
Melt Massflowrate (5kg), G/10min | 0.30 ± 0.06 | 0.31 | Q/SY DS 0507 |
Ketumpatan, kg/mā | 960 ± 2 | 959.7 | ISO 1183-2 |
Tensileyieldstress, MPA | ≥21.0 | 22.2 | Q/SY DS 0501 |
Tensilestrain atbreak, % | ≥350 | 770 | Q/SY DS 0501 |
Charpy ImpactStrength, kJ/m^2 | ≥22.0 | 27.2 | Q/SY DS 0503 |
Penyebaran hitam karbon, sizeclass | ≤3 | 2.3 | Q/SY DS 0508 |
Masa induksi pengoksidaan (isothermal OIT) (210 ℃), min | ≥20 | 60.7 | GB/T 19466.6-2009 |
Kandungan Hitam Karbon, M/M% | 2.0-2.5 | 2.17 | GB 13021-1991 |
Kelembapan, % | Diukur | 0.006 | SH/T 1770-2010 |
| | | |
| | |