| PE100 | 10 MPa |
| Maombi | Tube ya PE, bomba la gesi |
Bidhaa ya uchambuzi | Faharisi ya ubora | Matokeo ya mtihani | Njia ya mtihani |
Kuyeyuka Massflowrate (5kg), g/10min | 0.30 ± 0.06 | 0.31 | Q/SY DS 0507 |
Uzani, kilo/mā | 960 ± 2 | 959.7 | ISO 1183-2 |
Tensileyieldstress, MPA | ≥21.0 | 22.2 | Q/SY DS 0501 |
Tensilestrain atbreak, % | ≥350 | 770 | Q/SY DS 0501 |
Charpy ImpactStrength, KJ/M^2 | ≥22.0 | 27.2 | Q/SY DS 0503 |
Kutawanyika kwa kaboni nyeusi, sizeclass | ≤3 | 2.3 | Q/SY DS 0508 |
Wakati wa induction ya oxidation (Isothermal OIT) (210 ℃), min | ≥20 | 60.7 | GB/T 19466.6-2009 |
Yaliyomo nyeusi ya kaboni, m/m% | 2.0-2.5 | 2.17 | GB 13021-1991 |
Unyevu, % | Kipimo | 0.006 | SH/T 1770-2010 |
 |  |  |  |
 |  |  |
| PE100 | 10 MPa |
| Maombi | Tube ya PE, bomba la gesi |
Bidhaa ya uchambuzi | Faharisi ya ubora | Matokeo ya mtihani | Njia ya mtihani |
Kuyeyuka Massflowrate (5kg), g/10min | 0.30 ± 0.06 | 0.31 | Q/SY DS 0507 |
Uzani, kilo/mā | 960 ± 2 | 959.7 | ISO 1183-2 |
Tensileyieldstress, MPA | ≥21.0 | 22.2 | Q/SY DS 0501 |
Tensilestrain atbreak, % | ≥350 | 770 | Q/SY DS 0501 |
Charpy ImpactStrength, KJ/M^2 | ≥22.0 | 27.2 | Q/SY DS 0503 |
Kutawanyika kwa kaboni nyeusi, sizeclass | ≤3 | 2.3 | Q/SY DS 0508 |
Wakati wa induction ya oxidation (Isothermal OIT) (210 ℃), min | ≥20 | 60.7 | GB/T 19466.6-2009 |
Yaliyomo nyeusi ya kaboni, m/m% | 2.0-2.5 | 2.17 | GB 13021-1991 |
Unyevu, % | Kipimo | 0.006 | SH/T 1770-2010 |
| | | |
| | |