| PE100 | 10 MPa |
| Toepassing | PE -buis, gaspyp |
Analise -item |
Kwaliteit -indeks |
Toetsresultaat |
Toetsmetode |
Smeltmassflowrate (5 kg), g/10min |
0,30 ± 0,06 |
0.31 |
Q/SY DS 0507 |
Digtheid, kg/mā |
960 ± 2 |
959.7 |
ISO 1183-2 |
Tensileyieldstres, MPA |
≥21.0 |
22.2 |
Q/SY DS 0501 |
Tensilestrain atbreak, % |
≥350 |
770 |
Q/SY DS 0501 |
Charpy ImpactStrength, Kj/M^2 |
≥22.0 |
27.2 |
Q/SY DS 0503 |
Koolstof swart verspreiding, sizeclass |
≤3 |
2.3 |
Q/SY DS 0508 |
Oksidasie -induksietyd (Isotermiese OIT) (210 ℃), min |
≥20 |
60.7 |
GB/T 19466.6-2009 |
Koolstof swart inhoud, m/m% |
2.0-2.5 |
2.17 |
GB 13021-1991 |
Vog, % |
Gemeet |
0.006 |
SH/T 1770-2010 |
 |
 |
 |
 |
 |
 |
 |
| PE100 | 10 MPa |
| Toepassing | PE -buis, gaspyp |
Analise -item |
Kwaliteit -indeks |
Toetsresultaat |
Toetsmetode |
Smeltmassflowrate (5 kg), g/10min |
0,30 ± 0,06 |
0.31 |
Q/SY DS 0507 |
Digtheid, kg/mā |
960 ± 2 |
959.7 |
ISO 1183-2 |
Tensileyieldstres, MPA |
≥21.0 |
22.2 |
Q/SY DS 0501 |
Tensilestrain atbreak, % |
≥350 |
770 |
Q/SY DS 0501 |
Charpy ImpactStrength, Kj/M^2 |
≥22.0 |
27.2 |
Q/SY DS 0503 |
Koolstof swart verspreiding, sizeclass |
≤3 |
2.3 |
Q/SY DS 0508 |
Oksidasie -induksietyd (Isotermiese OIT) (210 ℃), min |
≥20 |
60.7 |
GB/T 19466.6-2009 |
Koolstof swart inhoud, m/m% |
2.0-2.5 |
2.17 |
GB 13021-1991 |
Vog, % |
Gemeet |
0.006 |
SH/T 1770-2010 |
|
|
|
|
|
|
|