| Kuantitas: | |
|---|---|
| PE100 | 10 MPa |
| Aplikasi | Tabung PE, pipa gas |
Item analisis | Indeks kualitas | Hasil tes | Metode pengujian |
Melt Massflowrate (5kg), G/10 menit | 0,30 ± 0,06 | 0.31 | Q/Sy DS 0507 |
Kepadatan, kg/mā | 960 ± 2 | 959.7 | ISO 1183-2 |
TENSILEYIELDSTRESS, MPA | ≥21.0 | 22.2 | Q/Sy DS 0501 |
Atbreak tensilestrain, % | ≥350 | 770 | Q/Sy DS 0501 |
Charpy ImpactStrength, kJ/m^2 | ≥22.0 | 27.2 | Q/Sy DS 0503 |
Dispersi karbon hitam, sizeclass | ≤3 | 2.3 | Q/Sy DS 0508 |
Waktu induksi oksidasi (isotermal OIT) (210 ℃), min | ≥20 | 60.7 | GB/T 19466.6-2009 |
Kandungan karbon hitam, m/m% | 2.0-2.5 | 2.17 | GB 13021-1991 |
Kelembaban, % | Diukur | 0.006 | SH/T 1770-2010 |
 |  |  |  |
 |  |  |
| PE100 | 10 MPa |
| Aplikasi | Tabung PE, pipa gas |
Item analisis | Indeks kualitas | Hasil tes | Metode pengujian |
Melt Massflowrate (5kg), G/10 menit | 0,30 ± 0,06 | 0.31 | Q/Sy DS 0507 |
Kepadatan, kg/mā | 960 ± 2 | 959.7 | ISO 1183-2 |
TENSILEYIELDSTRESS, MPA | ≥21.0 | 22.2 | Q/Sy DS 0501 |
Atbreak tensilestrain, % | ≥350 | 770 | Q/Sy DS 0501 |
Charpy ImpactStrength, kJ/m^2 | ≥22.0 | 27.2 | Q/Sy DS 0503 |
Dispersi karbon hitam, sizeclass | ≤3 | 2.3 | Q/Sy DS 0508 |
Waktu induksi oksidasi (isotermal OIT) (210 ℃), min | ≥20 | 60.7 | GB/T 19466.6-2009 |
Kandungan karbon hitam, m/m% | 2.0-2.5 | 2.17 | GB 13021-1991 |
Kelembaban, % | Diukur | 0.006 | SH/T 1770-2010 |
| | | |
| | |