| Kuantitas: | |
|---|---|
| PE100 | 10 MPa |
| Aplikasi | Tabung pe |
Barang |
Satuan |
Indeks kualitas |
Metode pengujian |
Mfr |
g/10 menit |
0.26-0.44 |
0.27 |
Kekuatan tarik saat dihasilkan |
MPa |
≥23.0 |
24.2 |
Modulus tarik |
MPa |
≥960 |
990 |
Regangan nominal fraktur tarik |
% |
≥5.5 × 10^2 |
5.9 × 10^2 |
Kepadatan |
g/cm^3 |
0,9600 ± 0,0030 |
0.9600 |
| OIT (210 ℃) | Min |
≥25 |
45.1 |
 |
 |
 |
 |
 |
 |
 |
| PE100 | 10 MPa |
| Aplikasi | Tabung pe |
Barang |
Satuan |
Indeks kualitas |
Metode pengujian |
Mfr |
g/10 menit |
0.26-0.44 |
0.27 |
Kekuatan tarik saat dihasilkan |
MPa |
≥23.0 |
24.2 |
Modulus tarik |
MPa |
≥960 |
990 |
Regangan nominal fraktur tarik |
% |
≥5.5 × 10^2 |
5.9 × 10^2 |
Kepadatan |
g/cm^3 |
0,9600 ± 0,0030 |
0.9600 |
| OIT (210 ℃) | Min |
≥25 |
45.1 |
|
|
|
|
|
|
|