| Cainníocht: | |
|---|---|
| PE100 | 10 MPa |
| Iarrchán | Feadán corp |
Mír |
Aonad |
Innéacs ardchaighdeáin |
Modh tástáil |
MFR |
g/10min |
0.26-0.44 |
0.27 |
Neart teanntachta ag an toradh |
MPA |
≥23.0 |
24.2 |
Modulus teanntachta |
MPA |
≥960 |
990 |
Brú ainmniúil briste teanntachta |
% |
≥5.5 × 10^2 |
5.9 × 10^2 |
Dlús |
g/cm^3 |
0.9600 ± 0.0030 |
0.9600 |
| OIT (210 ℃) | Mí Miannach |
≥25 |
45.1 |
 |
 |
 |
 |
 |
 |
 |
| PE100 | 10 MPa |
| Iarrchán | Feadán corp |
Mír |
Aonad |
Innéacs ardchaighdeáin |
Modh tástáil |
MFR |
g/10min |
0.26-0.44 |
0.27 |
Neart teanntachta ag an toradh |
MPA |
≥23.0 |
24.2 |
Modulus teanntachta |
MPA |
≥960 |
990 |
Brú ainmniúil briste teanntachta |
% |
≥5.5 × 10^2 |
5.9 × 10^2 |
Dlús |
g/cm^3 |
0.9600 ± 0.0030 |
0.9600 |
| OIT (210 ℃) | Mí Miannach |
≥25 |
45.1 |
|
|
|
|
|
|
|