| PE100 | 10 MPa |
| Taupānga | ngongo PE |
Tūemi |
Waeine |
Taurangi Kounga |
Tikanga whakamatautau |
MFR |
g/10 min |
0.26-0.44 |
0.27 |
Te Kaha Tensile i te tuku |
MPa |
≥23.0 |
24.2 |
Kōwae Tensile |
MPa |
≥960 |
990 |
Te Riki Whakaingonga Tangata Whati |
% |
≥5.5×10^2 |
5.9×10^2 |
Kiato |
g/cm^3 |
0.9600±0.0030 |
0.9600 |
| OIT(210 ℃) | Min |
≥25 |
45.1 |
 |
 |
 |
 |
 |
 |
 |