| Pe100 | X MPA |
| Applicatio | Pe tubo |
Item |
Unitas |
Index |
Test modus |
MFR |
G / 10min |
0,26-0.44 |
0.27 |
Tensile vires ad cede |
MPA |
≥23.0 |
24.2 |
Tensile modulus |
MPA |
≥960 |
990 |
Tensile fractura nominis iactabantur |
% |
≥5.5 × X ^ II |
5.9 × X ^ II |
Densitas |
G / III cm ^ |
0.9600 ± 0.0030 |
0.9600 |
| Oit (CCX ℃) | Min |
≥25 |
45.1 |
 |
 |
 |
 |
 |
 |
 |
| Pe100 | X MPA |
| Applicatio | Pe tubo |
Item |
Unitas |
Index |
Test modus |
MFR |
G / 10min |
0,26-0.44 |
0.27 |
Tensile vires ad cede |
MPA |
≥23.0 |
24.2 |
Tensile modulus |
MPA |
≥960 |
990 |
Tensile fractura nominis iactabantur |
% |
≥5.5 × X ^ II |
5.9 × X ^ II |
Densitas |
G / III cm ^ |
0.9600 ± 0.0030 |
0.9600 |
| Oit (CCX ℃) | Min |
≥25 |
45.1 |
|
|
|
|
|
|
|