Pe100 | X MPA |
Applicatio | Pe tubo |
Analysis Item | Index | TRIEN | Test modus |
Nigra macula grana et colore grana | ≤10 | 5 | SH / T1541.1 |
Meltere massa fluxus rate g / 10min | 0.20-0.26 | 0.22 | GB / T3682.1-201-2018 |
Density G / cm ^ III | 0.9470-0.9530 | 0.9477 | GB / T1033.2 |
Tensile cede accentus, MPA | ≥20 | 21.4 | GB / T1040.2 |
Tensile confractus nominis iactabantur,% | ≥500 | 836 | GB / T1040.2 |
Flexural modulum | ≥700 | 1044 | GB / T9341 |
Oxidatio inductione tempore | ≥40 | 6 | GB / T 19466.6-2009 |
Volatile contentus, mg / kg | ≤300 | 74 | GB / T 15558.1-2015 |
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Pe100 | X MPA |
Applicatio | Pe tubo |
Analysis Item | Index | TRIEN | Test modus |
Nigra macula grana et colore grana | ≤10 | 5 | SH / T1541.1 |
Meltere massa fluxus rate g / 10min | 0.20-0.26 | 0.22 | GB / T3682.1-201-2018 |
Density G / cm ^ III | 0.9470-0.9530 | 0.9477 | GB / T1033.2 |
Tensile cede accentus, MPA | ≥20 | 21.4 | GB / T1040.2 |
Tensile confractus nominis iactabantur,% | ≥500 | 836 | GB / T1040.2 |
Flexural modulum | ≥700 | 1044 | GB / T9341 |
Oxidatio inductione tempore | ≥40 | 6 | GB / T 19466.6-2009 |
Volatile contentus, mg / kg | ≤300 | 74 | GB / T 15558.1-2015 |
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |