| Pe80 | VIII MPA |
| Applicatio | Pe tubo |
Analysis Item | Index | TRIEN | Test modus |
Nigra macula grana et colore grana | ≤10 | 0 | SH / T 1541.1-2019 |
Missam fluxus rate (21.6kg), G / 10min | XI ± III | 10 | GB / T 3682.1-2018 |
Density, G / cm ^ III | 0.945 ± 0.003 | 0.947 | GB / T 1033.2-2010 |
Tensile cede accentus, MPA | ≥18.0 | 22.2 | GB / T 1040.2-2006 |
Tensile nominis iactabantur ad confractus,% | ≥350 | 609 | GB / T 1040.2-2006 |
| Charypy Notched Impact fortitudinem (XXIII ° F) .kj / m ^ II | ≥450 | 859 | GB / T 1043.1-2008 |
| Oxidatio inductione tempore | ≥20 | 87 | GB / T 19466.6-2009 |
 |  |  |  |
 |  |  |
| Pe80 | VIII MPA |
| Applicatio | Pe tubo |
Analysis Item | Index | TRIEN | Test modus |
Nigra macula grana et colore grana | ≤10 | 0 | SH / T 1541.1-2019 |
Missam fluxus rate (21.6kg), G / 10min | XI ± III | 10 | GB / T 3682.1-2018 |
Density, G / cm ^ III | 0.945 ± 0.003 | 0.947 | GB / T 1033.2-2010 |
Tensile cede accentus, MPA | ≥18.0 | 22.2 | GB / T 1040.2-2006 |
Tensile nominis iactabantur ad confractus,% | ≥350 | 609 | GB / T 1040.2-2006 |
| Charypy Notched Impact fortitudinem (XXIII ° F) .kj / m ^ II | ≥450 | 859 | GB / T 1043.1-2008 |
| Oxidatio inductione tempore | ≥20 | 87 | GB / T 19466.6-2009 |
| | | |
| | |