Features | high gloss, medium impact resistance, high rigidity and versatility |
Application | toys, household appliances, office supplies, automotive applications, electrical applications, small household appliances, automotive external parts, automotive internal parts |
Analysis Item | Qualified product | Test result | Test method | |
Granular appearance | Natural color particles no impurities | impurities | Visual method | |
Flake Stain, 10g | ≤ | 15 | 4 | Q/SY 03063-2019 |
Large grain, g/kg | ≤ | 5 | 0.5 | SH/T 1541.1 |
Small grains, g/kg | ≤ | 5 | 0.3 | SH/T 1541.1 |
Melt mass flow Rate, g/10min | 18.0~24.0 | 22 | GB/T 3682.1-2018 | |
Tensilestrength, MPa | ≥ | 43.0 | 44.0 | GB/T 1040.2-2006 |
Bending strength, MPa | ≥ | 71.0 | 73.5 | GB/T 9341-2008 |
Flexural modulusofelasticity, MPa | ≥ | 2300 | 2465 | GB/T 9341-2008 |
Charpy notched impactstrength, kJ/m^2 | ≥ | 16.0 | 19.6 | GB/T 1043.1-2008 |
Vicat softening temperature, °C | ≥ | 92.0 | 95.5 | GB/T 1633-2000 |
Rockwell hardness,(R ruler) | ≥ | 107 | 110 | GB/T 3398.2-2008 |
Yellow index | ≤ | 30.0 | 23.8 | HG/T 3862-2006 |
Whiteness | ≥ | 58.0 | 61.7 | GB/T 2913-1982 |
![]() | ![]() | ![]() |
Features | high gloss, medium impact resistance, high rigidity and versatility |
Application | toys, household appliances, office supplies, automotive applications, electrical applications, small household appliances, automotive external parts, automotive internal parts |
Analysis Item | Qualified product | Test result | Test method | |
Granular appearance | Natural color particles no impurities | impurities | Visual method | |
Flake Stain, 10g | ≤ | 15 | 4 | Q/SY 03063-2019 |
Large grain, g/kg | ≤ | 5 | 0.5 | SH/T 1541.1 |
Small grains, g/kg | ≤ | 5 | 0.3 | SH/T 1541.1 |
Melt mass flow Rate, g/10min | 18.0~24.0 | 22 | GB/T 3682.1-2018 | |
Tensilestrength, MPa | ≥ | 43.0 | 44.0 | GB/T 1040.2-2006 |
Bending strength, MPa | ≥ | 71.0 | 73.5 | GB/T 9341-2008 |
Flexural modulusofelasticity, MPa | ≥ | 2300 | 2465 | GB/T 9341-2008 |
Charpy notched impactstrength, kJ/m^2 | ≥ | 16.0 | 19.6 | GB/T 1043.1-2008 |
Vicat softening temperature, °C | ≥ | 92.0 | 95.5 | GB/T 1633-2000 |
Rockwell hardness,(R ruler) | ≥ | 107 | 110 | GB/T 3398.2-2008 |
Yellow index | ≤ | 30.0 | 23.8 | HG/T 3862-2006 |
Whiteness | ≥ | 58.0 | 61.7 | GB/T 2913-1982 |
![]() | ![]() | ![]() |