| Features | high impact resistance |
| Application | toys, washing machines, air conditioners, electrical applications, external parts of automobiles and internal parts of automobiles |
Item | Quality Index | Test result | Test method | |
Appearance | Natural color particles, no impurities | Natural color par no impurities | JH318.10207.004-2022 | |
Flake Stain, 10g | ≤ | 9 | 4 | Q/SY 03063—2019 |
Melt mass flow rate g/10min | 18.0～24.0 | 20.6 | GB/T 3682.1-2018 | |
Tensile strength, MPa | ≥ | 41.0 | 45.4 | GB/T 1040.2-2006 |
Bending strength MPa | ≥ | 68.0 | 71.1 | GB/T 9341-2008 |
Flexural modulus of elasticity, MPa | ≥ | 2200 | 2235 | GB/T 9341-2008 |
| Charpy notched impact strength, KJ/m2 | ≥ | 18.0 | 22.6 | GB/T 1043.1-2008 |
| Vicat softening temperature, ℃ | ≥ | 90.0 | 96.9 | GB/T 1633-2000 |
| Yellow index | ≤ | 25.0 | 21.5 | HG/T 3862-2006 |
| Whiteness | ≥ | 63.0 | 64.9 | GB/T 2913-1982 |
| Rockwell hardness, R scale | ≥ | 105 | 105 | GB/T 3398.2-2008 |
|
|
|
 |  |  |
| Features | high impact resistance |
| Application | toys, washing machines, air conditioners, electrical applications, external parts of automobiles and internal parts of automobiles |
Item | Quality Index | Test result | Test method | |
Appearance | Natural color particles, no impurities | Natural color par no impurities | JH318.10207.004-2022 | |
Flake Stain, 10g | ≤ | 9 | 4 | Q/SY 03063—2019 |
Melt mass flow rate g/10min | 18.0～24.0 | 20.6 | GB/T 3682.1-2018 | |
Tensile strength, MPa | ≥ | 41.0 | 45.4 | GB/T 1040.2-2006 |
Bending strength MPa | ≥ | 68.0 | 71.1 | GB/T 9341-2008 |
Flexural modulus of elasticity, MPa | ≥ | 2200 | 2235 | GB/T 9341-2008 |
| Charpy notched impact strength, KJ/m2 | ≥ | 18.0 | 22.6 | GB/T 1043.1-2008 |
| Vicat softening temperature, ℃ | ≥ | 90.0 | 96.9 | GB/T 1633-2000 |
| Yellow index | ≤ | 25.0 | 21.5 | HG/T 3862-2006 |
| Whiteness | ≥ | 63.0 | 64.9 | GB/T 2913-1982 |
| Rockwell hardness, R scale | ≥ | 105 | 105 | GB/T 3398.2-2008 |
|
|
|
| | |