| Features | Toughening, high fluidity and versatility |
| Application | Electrical components, automotive applications, electrical applications |
Analysis Item | Quality Index | Results of testing | Experiment method (standardencdoing) |
Appearance | Natural color particles, no impurities | Natural color par no impurities | ticles, SH/T 1541.1-2019 |
Izod impact strength J/M | ≥167 | 251 | ASTM D256-2010 |
Tensile strength MPa | ≥42 | 50 | ASTM D638-2010 |
Melt mass flow rate g/10min | 25-36 | 31 | GB/T 3682.1-2018 |
Rockwell hardness, R scale | ≥100 | 110 | ASTM D785-2008 |
Heat distortion temperature, | ≥78 | 80 | ASTM D648-2007 |
Bending strength MPa | ≥60 | 66 | ASTM D790-2010 |
Flexural modulus of elasticity, MPa | ≥1900 | 2227 | ASTM D790-2010 |
Large granules,g/kg | ≤5 | 0 | SH/T 1541.1-2019 |
| Small granules,g/kg | ≤5 | 0 | SH/T 1541.1-2019 |
 |  |  |
 |  |  |
| Features | Toughening, high fluidity and versatility |
| Application | Electrical components, automotive applications, electrical applications |
Analysis Item | Quality Index | Results of testing | Experiment method (standardencdoing) |
Appearance | Natural color particles, no impurities | Natural color par no impurities | ticles, SH/T 1541.1-2019 |
Izod impact strength J/M | ≥167 | 251 | ASTM D256-2010 |
Tensile strength MPa | ≥42 | 50 | ASTM D638-2010 |
Melt mass flow rate g/10min | 25-36 | 31 | GB/T 3682.1-2018 |
Rockwell hardness, R scale | ≥100 | 110 | ASTM D785-2008 |
Heat distortion temperature, | ≥78 | 80 | ASTM D648-2007 |
Bending strength MPa | ≥60 | 66 | ASTM D790-2010 |
Flexural modulus of elasticity, MPa | ≥1900 | 2227 | ASTM D790-2010 |
Large granules,g/kg | ≤5 | 0 | SH/T 1541.1-2019 |
| Small granules,g/kg | ≤5 | 0 | SH/T 1541.1-2019 |
| | |
| | |