| Features | Oleum resistentia et senescit resistentia |
| Applicationem | Cum bono frigore resistentia, resistentia gerunt, humilis calor et generatio et alta elasticitas, bonum senescit resistentia, amplis est synthetica generalis Flexilis. Maxime adhibetur ut calcationem, cingulum, cingulum, transmissionem, cingulum, tenaces pannum, unicum, et sic deinceps, post emundationem machinae naturalis. |
Item |
Index |
Test eventus |
Test modus |
||
Ego typus |
type | type |
|||
Aspectus |
Color levis et translucens, figura primaria est scandalum, non continet particulas coctas, sordes mechanicas et maculas olei. |
Visual inspectionem |
|||
Materia volatilis, % (fraction massa) |
≤0.50 |
≤0.80 | ≤1.10 |
0.29 |
GB/T 24131.1-2018 Methodus calidi cylindri |
viscositas lunae rudis rubber［ML(1+4) 100℃］ |
45±4 |
45±5 | 45±7 | 45 |
GB/T 1232.1-2016Direct methodus, si aspera cylindro, temperatura 35℃±5℃ |
Cinis contentus,% (fractio massa) |
≤0.20 |
≤0.20 | ≤0.20 | 0.19 | GB/T 4498.1-2013 Method A |
Flexilis Money viscositas mixta ML(1+4)10℃］ |
≤65 |
≤67 | ≤70 | 56 |
GB/T 8660-2018（C2mixtio methodi GB/T 1232.1-2016 |
CCC% Definite accentus (145℃， 25min), MPa |
7.0～12.0 |
7.0～12.0 | 7.0～12.0 |
9.5 |
Misce secundum GB/T 8660-2018, C2 modum, metire secundum GB/T528-2009, utere typus I cutter. |
CCC% Definite accentus (145℃, 35min), MPa |
8.0～13.0 |
8.0～13.0 | 8.0～13.0 | 9.7 |
|
300% Definite accentus (145℃, 50min) MPa |
8.0～13.0 |
8.0～13.0 | 8.0～13.0 |
9.8 |
|
Tensile Strength（145℃,35min）,MPa |
≥13.2 |
≥13.2 | ≥13.2 |
14.3 | |
Prolongatio ad intermissum（145℃, 35min）,% |
≥330 |
≥330 | ≥330 |
377 | |
| Vulcanization possessiones 160℃，25min）ML,dN·m | Report | Report | Report | 2.5 | Parametros pone secundum GB/T 8660-2018 7.2, et metire secundum GB/T 8660-2018（C2mixtionem methodi GB/T 1232.1-2016 ad GB/T25268-2010. |
| Proprietates Vulcanizationis,160℃，25min,MH,dN·m | Report | Report | Report | 18.6 | |
| Proprietates Vulcanizationis, 160 ℃， 25min, ts1, min | Report | Report | Report | 3.0 | |
| Vulcanization proprietatibus, 160 ℃， 25min, tc50, min | Report | Report | Report | 6.3 | |
| Vulcanization possessiones, 160 ℃， 25min, tc90, min | Report | Report | Report | 10.4 | |
|
|
|
 |
 |
 |