Features | facile ad processum |
Applicatio | Oleum-extenditur styrene-butadiene Flexilis, propter calcantum Flexilis, TRADUCTOR balteus et caligarum de viatoribus currus rotae |
Item |
Index |
Test modus |
Res |
Conclusio |
|
Superior productio |
Qualified uber |
||||
Species |
Non-polluat obstructionum lucis coloris gluten, liberi de cocking particulas, harenae et mechanica impudicitiis. |
Visus |
Normalis |
Superior |
|
Volatile (%) ≤ |
0.60 |
0.60 |
GB / T 24131.1- MMXVIII, calidum volumine Ratio B2 |
0.13 |
Superior |
Organicum acidum (%) |
3.90 ~ 5.7 |
GB / T 8657- MMXIV, B ratio |
4.66 |
Superior |
|
Soap content (%) ≤ |
0.50 |
0.16 |
Superior |
||
Tenetur styrene (%) |
22.5 ~ 24.5 |
GB / T 8658-1998 |
23.4 |
Superior |
|
Rudis rubber Moneoney Viscosity , Ml (I + IV) C ℃ |
XLIV LIV |
XLIV LVI |
GB / T 1232.1- MMXVI, super Roll Methodo |
L XLIX L |
Superior |
Monone Viscositas compositis: Ml (I + IV) C ℃ ≤ |
70 |
GB / T 1232.1- MMXVI (ASTM IRB No.8) |
58 |
Superior |
|
CCC% accentus ad modulus (CXLV ℃, 35min) (MPA) |
8.8 |
12.8 |
GB / T 8656-2018 A (ASTM IRB No.8): GB / T 528-2009 (I Conscidisti cultro) |
9.2 |
Superior |
Tensile vires (CXLV ℃, 35min) (MPa) ≥ |
19.4 |
19.4 |
20.7 |
Superior |
|
Elongatio ad confractus (CXLV ℃, 35min) (%) ≥ |
460 |
460 |
588 |
Superior |
![]() |
![]() |
![]() |
Features | facile ad processum |
Applicatio | Oleum-extenditur styrene-butadiene Flexilis, propter calcantum Flexilis, TRADUCTOR balteus et caligarum de viatoribus currus rotae |
Item |
Index |
Test modus |
Res |
Conclusio |
|
Superior productio |
Qualified uber |
||||
Species |
Non-polluat obstructionum lucis coloris gluten, liberi de cocking particulas, harenae et mechanica impudicitiis. |
Visus |
Normalis |
Superior |
|
Volatile (%) ≤ |
0.60 |
0.60 |
GB / T 24131.1- MMXVIII, calidum volumine Ratio B2 |
0.13 |
Superior |
Organicum acidum (%) |
3.90 ~ 5.7 |
GB / T 8657- MMXIV, B ratio |
4.66 |
Superior |
|
Soap content (%) ≤ |
0.50 |
0.16 |
Superior |
||
Tenetur styrene (%) |
22.5 ~ 24.5 |
GB / T 8658-1998 |
23.4 |
Superior |
|
Rudis rubber Moneoney Viscosity , Ml (I + IV) C ℃ |
XLIV LIV |
XLIV LVI |
GB / T 1232.1- MMXVI, super Roll Methodo |
L XLIX L |
Superior |
Monone Viscositas compositis: Ml (I + IV) C ℃ ≤ |
70 |
GB / T 1232.1- MMXVI (ASTM IRB No.8) |
58 |
Superior |
|
CCC% accentus ad modulus (CXLV ℃, 35min) (MPA) |
8.8 |
12.8 |
GB / T 8656-2018 A (ASTM IRB No.8): GB / T 528-2009 (I Conscidisti cultro) |
9.2 |
Superior |
Tensile vires (CXLV ℃, 35min) (MPa) ≥ |
19.4 |
19.4 |
20.7 |
Superior |
|
Elongatio ad confractus (CXLV ℃, 35min) (%) ≥ |
460 |
460 |
588 |
Superior |
![]() |
![]() |
![]() |