| Applicatio | In line with the requirements of the European Union environmental protection butadiene rubber, used for automotive, drilling, engineering hydraulic hose in the rubber layer, the inner layer, textile rubber appearance, printing rubber,fitness material and translucent business material protection control materials and other insulation foaming materials, oil tank lining, oil resistant seal and miscellany. |
Analysis Item | Qualitas iAndex | Test results | Experimentum modum | |
Superior productio | Qualified uber | |||
Volatile materia,% (missa fraction) | ≤0.50 | ≤0.70 | 0.18 | GB / T 24131.1-2018 Hot Roller Ratio B2 |
Fraxinus contentus,% (missa fraction) | ≤0.75 | ≤0.75 | 0.71 | GB / T 4498.1-2013 |
Alligatus acryonitrile,% (missa fraction) | 32.5 ~ 34,5 | 31.5 ~ 34.5 | 34.4 | SH / T 1157.2-2015: A |
Viscositas Mononey, ml (I + IV) C ° C | L ~ LX | L ~ LX | 55 | GB / T 15340-2008 super Roll Modus GB / T1232.1 |
CCC% modulus accentus (CXLV ℃, 50min Typus I Sample, celeritate 500mm / min), MPA | 10,6 ~ 14.6 | 10.3 ~ 14.9 | 12.7 | GB / T 34685-2017 ASTM IRB non VIII Carbon Nigrum GB / T 528-2009 Typus ego dutter |
Tensile fortitudo (CXLV ° C, 50min Type EGO Sample, celeritate 500mm / min), MPA | ≥25 | ≥24 | 30.4 | |
Elongatio ad confractus (CXLV ° C, 50min Type Ego Sample, celeritate 500mm / min),% | ≥470 | ≥440 | 595 | |
|
|
|
|
|
|
| Applicatio | In line with the requirements of the European Union environmental protection butadiene rubber, used for automotive, drilling, engineering hydraulic hose in the rubber layer, the inner layer, textile rubber appearance, printing rubber,fitness material and translucent business material protection control materials and other insulation foaming materials, oil tank lining, oil resistant seal and miscellany. |
Analysis Item | Qualitas iAndex | Test results | Experimentum modum | |
Superior productio | Qualified uber | |||
Volatile materia,% (missa fraction) | ≤0.50 | ≤0.70 | 0.18 | GB / T 24131.1-2018 Hot Roller Ratio B2 |
Fraxinus contentus,% (missa fraction) | ≤0.75 | ≤0.75 | 0.71 | GB / T 4498.1-2013 |
Alligatus acryonitrile,% (missa fraction) | 32.5 ~ 34,5 | 31.5 ~ 34.5 | 34.4 | SH / T 1157.2-2015, A |
Viscositas Mononey, ml (I + IV) C ° C | L ~ LX | L ~ LX | 55 | GB / T 15340-2008 super Roll Modus GB / T1232.1 |
CCC% modulus accentus (CXLV ℃, 50min Typus I Sample, celeritate 500mm / min), MPA | 10,6 ~ 14.6 | 10.3 ~ 14.9 | 12.7 | GB / T 34685-2017 ASTM IRB non VIII Carbon Nigrum GB / T 528-2009 Typus ego dutter |
Tensile fortitudo (CXLV ° C, 50min Type EGO Sample, celeritate 500mm / min), MPA | ≥25 | ≥24 | 30.4 | |
Elongatio ad confractus (CXLV ° C, 50min Type Ego Sample, celeritate 500mm / min),% | ≥470 | ≥440 | 595 | |
|
|
|
|
|
|