| Features | Oleum resistentia et senescentis resistentia |
| Applicatio | Cum bonis frigore resistentia, gerunt resistentia, humilis calor generatio et princeps elasticitate, bonum canus resistentia, est amplis syntheticum Flexilis. Est maxime solebat ad calcare, onerariis balteus, transmissionem balteus, tenaces panno, solus et sic post Purgato cum naturalibus apparatus. |
Item | Index | TRIEN | Test modus | ||
Ego typus | Ⅱ type | Ⅲ type | |||
Species | Lux et translucet, prima figura est obstructionum, non habet Coked particulas, mechanica impudicitiis et oleum maculas | Visual inspectionem | |||
Volatile materia,% (missa fraction) | ≤0.50 | ≤0.80 | ≤1.10 | 0.29 | GB / T 24131.1-2018 Hot Roller Ratio |
Viscositas Rudis Rudis Rudber [ML (I + IV) C ℃] | XLV ± IV | XLV ± V | XLV ± VII | 45 | GB / T 1232.1-2016Direct modus, si th aspera a cylindro, temperatus XXXV ℃ ± V ℃ |
Fraxinus contentus,% (missa fraction) | ≤0.20 | ≤0.20 | ≤0.20 | 0.19 | GB / T 4498.1-2013 modum a |
Mixta Flexilis Moneoney Viscosity [ml (I + IV) X ℃] | ≤65 | ≤67 | ≤70 | 56 | GB / T 8660-2018 (C2Mixing Methodo) GB / T 1232.1-2016 |
CCC% certis accentus (CXLV ℃, 25min), MPA | 7.0 ~ 12.0 | 7.0 ~ 12.0 | 7.0 ~ 12.0 | 9.5 | Misce secundum GB / T 8660-2018, C2 modum, mensura secundum GB / T528-2009, uti type ego dromon. |
CCC% certis accentus (CXLV ℃, 35min), MPA | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 9.7 | |
CCC% certis accentus (CXLV ℃, 50min) MPA | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 9.8 | |
Tensile fortitudo (CXLV ℃, 35min), MPA | ≥13.2 | ≥13.2 | ≥13.2 | 14.3 | |
Elongatio ad confractus (CXLV ℃, 35min),% | ≥330 | ≥330 | ≥330 | 377 | |
| Vulcanization proprietatibus CLX ℃, 25min) ml, Dn · M | Report | Report | Report | 2.5 | Set parametri secundum GB / T 8660-2018 7.2, et mensura secundum GB / T 8660-2018 (C2Mixing Method) GB / T 1232.1-2016 GB / T25268-2010. |
| Vulcanization proprietatibus, CLX ℃, 25min, MH, DN · M | Report | Report | Report | 18.6 | |
| Vulcanization proprietatibus, CLX ℃, 25min, ts1, min | Report | Report | Report | 3.0 | |
| Vulcanization proprietatibus, CLX ℃, 25min, TC50, min | Report | Report | Report | 6.3 | |
| Vulcanization proprietatibus, CLX ℃, 25min, TC90, min | Report | Report | Report | 10.4 | |
|
|
|
 |  |  |
| Features | Oleum resistentia et senescentis resistentia |
| Applicatio | Cum bonis frigore resistentia, gerunt resistentia, humilis calor generatio et princeps elasticitate, bonum canus resistentia, est amplis syntheticum Flexilis. Est maxime solebat ad calcare, onerariis balteus, transmissionem balteus, tenaces panno, solus et sic post Purgato cum naturalibus apparatus. |
Item | Index | TRIEN | Test modus | ||
Ego typus | Ⅱ type | Ⅲ type | |||
Species | Lux et translucet, prima figura est obstructionum, non habet Coked particulas, mechanica impudicitiis et oleum maculas | Visual inspectionem | |||
Volatile materia,% (missa fraction) | ≤0.50 | ≤0.80 | ≤1.10 | 0.29 | GB / T 24131.1-2018 Hot Roller Ratio |
Viscositas Rudis Rudis Rudber [ML (I + IV) C ℃] | XLV ± IV | XLV ± V | XLV ± VII | 45 | GB / T 1232.1-2016Direct modus, si th aspera a cylindro, temperatus XXXV ℃ ± V ℃ |
Fraxinus contentus,% (missa fraction) | ≤0.20 | ≤0.20 | ≤0.20 | 0.19 | GB / T 4498.1-2013 modum a |
Mixta Flexilis Moneoney Viscosity [ml (I + IV) X ℃] | ≤65 | ≤67 | ≤70 | 56 | GB / T 8660-2018 (C2Mixing Methodo) GB / T 1232.1-2016 |
CCC% certis accentus (CXLV ℃, 25min), MPA | 7.0 ~ 12.0 | 7.0 ~ 12.0 | 7.0 ~ 12.0 | 9.5 | Misce secundum GB / T 8660-2018, C2 modum, mensura secundum GB / T528-2009, uti type ego dromon. |
CCC% certis accentus (CXLV ℃, 35min), MPA | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 9.7 | |
CCC% certis accentus (CXLV ℃, 50min) MPA | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 8.0 ~ 13.0 | 9.8 | |
Tensile fortitudo (CXLV ℃, 35min), MPA | ≥13.2 | ≥13.2 | ≥13.2 | 14.3 | |
Elongatio ad confractus (CXLV ℃, 35min),% | ≥330 | ≥330 | ≥330 | 377 | |
| Vulcanization proprietatibus CLX ℃, 25min) ml, Dn · M | Report | Report | Report | 2.5 | Set parametri secundum GB / T 8660-2018 7.2, et mensura secundum GB / T 8660-2018 (C2Mixing Method) GB / T 1232.1-2016 GB / T25268-2010. |
| Vulcanization proprietatibus, CLX ℃, 25min, MH, DN · M | Report | Report | Report | 18.6 | |
| Vulcanization proprietatibus, CLX ℃, 25min, ts1, min | Report | Report | Report | 3.0 | |
| Vulcanization proprietatibus, CLX ℃, 25min, TC50, min | Report | Report | Report | 6.3 | |
| Vulcanization proprietatibus, CLX ℃, 25min, TC90, min | Report | Report | Report | 10.4 | |
|
|
|
| | |