| Applicatio | Est amet-amica nitrile Butadiene Flexilis in linea cum requisitis Europaeae unionem. Hoc adhibetur ad aedificationem, refrigerationem ratio et alia scelerisque insulatione spumans, oleum repugnans signing et miscellaneous partes, etc. |
Analysis Item | Qualitas iAndex | Test results | Experimentum modum | |
Superior productio | Qualified uber | |||
Volatile materia,% (missa fraction) | ≤0.50 | ≤0.70 | 0.18 | GB / T 24131.1-2018 Hot Roller Ratio B2 |
Fraxinus contentus,% (missa fraction) | ≤0.75 | ≤0.75 | 0.65 | GB / T 4498.1-2013 |
Alligatus acryonitrile,% (missa fraction) | 32.5 ~ 34,5 | 32.0 ~ 35.0 | 33.6 | SH / T 1157.2-2015: A |
Viscositas Mononey, ml (I + IV) C ° C | LXXV ~ LXXXV | LXXV ~ LXXXV | 81 | GB / T 15340-2008 super Roll Modus GB / T1232.1 |
CCC% modulus accentus (CXLV ℃, 50min Typus I Sample, celeritate 500mm / min), MPA | 10,4 ~ 14.4 | 10,1 ~ 14.7 | 13.4 | GB / T 34685-2017 ASTM IRB non VIII Carbon Nigrum GB / T 528-2009 Typus ego dutter |
Tensile fortitudo (CXLV ° C, 50min Type EGO Sample, celeritate 500mm / min), MPA | ≥26.4 | ≥25.3 | 28.9 | |
Elongatio ad confractus (CXLV ° C, 50min Type Ego Sample, celeritate 500mm / min),% | ≥490 | ≥460 | 546 | |
|
|
|
|
|
|
| Applicatio | Est amet-amica nitrile Butadiene Flexilis in linea cum requisitis Europaeae unionem. Hoc adhibetur ad aedificationem, refrigerationem ratio et alia scelerisque insulatione spumans, oleum repugnans signing et miscellaneous partes, etc. |
Analysis Item | Qualitas iAndex | Test results | Experimentum modum | |
Superior productio | Qualified uber | |||
Volatile materia,% (missa fraction) | ≤0.50 | ≤0.70 | 0.18 | GB / T 24131.1-2018 Hot Roller Ratio B2 |
Fraxinus contentus,% (missa fraction) | ≤0.75 | ≤0.75 | 0.65 | GB / T 4498.1-2013 |
Alligatus acryonitrile,% (missa fraction) | 32.5 ~ 34,5 | 32.0 ~ 35.0 | 33.6 | SH / T 1157.2-2015: A |
Viscositas Mononey, ml (I + IV) C ° C | LXXV ~ LXXXV | LXXV ~ LXXXV | 81 | GB / T 15340-2008 super Roll Modus GB / T1232.1 |
CCC% modulus accentus (CXLV ℃, 50min Typus I Sample, celeritate 500mm / min), MPA | 10,4 ~ 14.4 | 10,1 ~ 14.7 | 13.4 | GB / T 34685-2017 ASTM IRB non VIII Carbon Nigrum GB / T 528-2009 Typus ego dutter |
Tensile fortitudo (CXLV ° C, 50min Type EGO Sample, celeritate 500mm / min), MPA | ≥26.4 | ≥25.3 | 28.9 | |
Elongatio ad confractus (CXLV ° C, 50min Type Ego Sample, celeritate 500mm / min),% | ≥490 | ≥460 | 546 | |
|
|
|
|
|
|