| Puka tono | Ko te riipene Nitrile o te ao-a-taiao e pa ana ki nga whakaritenga o te Union Europi. Ka whakamahia hei hanga whare, te punaha pouaka whakaata me etahi atu whakatipu waiariki waiariki, he taapiri hinu-hinu me nga waahanga rereke, me etahi atu. |
Te tūemi Tātari | Te kounga Index | Nga kitenga whakamatautau | Tikanga whakamātautau | |
Tiketike hua | Hua Tohu | |||
Te take o te volatile,% (hautanga papatipu) | ≤0.50 | ≤0.70 | 0.18 | GB / T 24131.1-2018 Tikanga Roller Hot B2 |
Ihirangi pungarehu,% (hautanga papatipu) | ≤0.75 | ≤0.75 | 0.65 | GB / T 4498.1-2013 A |
Herea acrylonitrile,% (hautanga papatipu) | 32.5 ~ 34.5 | 32.0 ~ 35.0 | 33.6 | SH / T 1157.2-2015, Tikanga A |
Mooney Liscicoty, ML (1 + 4) 100 ° C | 75 ~ 85 | 75 ~ 85 | 81 | GB / T 15340-2008 Over Te tikanga o te GB / T1232.1 |
300% ahorangi modullus (145 ℃, 50intin Momo 1 tauira 1, tere 500mm / min), MPA | 10.4 ~ 14.4 | 10.1 ~ 14.7 | 13.4 | GB / T 34685-2017 Astm Irb no 8 karamu pango GB / T 528-2009 Patohia te tapahi i ahau |
Te kaha o te kaha (145 ° C, 505min Momo Tauira, Tere 500mm / min), MPA | ≥26.4 | ≥25.3 | 28.9 | |
Elngosation i te wa pakaru (145 ° C, 50min Momo i te tauira, tere 500mm / min),% | ≥490 | ≥460 | 546 | |
|
|
|
|
|
|
| Puka tono | Ko te riipene Nitrile o te ao-a-taiao e pa ana ki nga whakaritenga o te Union Europi. Ka whakamahia hei hanga whare, te punaha pouaka whakaata me etahi atu whakatipu waiariki waiariki, he taapiri hinu-hinu me nga waahanga rereke, me etahi atu. |
Te tūemi Tātari | Te kounga Index | Nga kitenga whakamatautau | Tikanga whakamātautau | |
Tiketike hua | Hua Tohu | |||
Te take o te volatile,% (hautanga papatipu) | ≤0.50 | ≤0.70 | 0.18 | GB / T 24131.1-2018 Tikanga Roller Hot B2 |
Ihirangi pungarehu,% (hautanga papatipu) | ≤0.75 | ≤0.75 | 0.65 | GB / T 4498.1-2013 A |
Herea acrylonitrile,% (hautanga papatipu) | 32.5 ~ 34.5 | 32.0 ~ 35.0 | 33.6 | SH / T 1157.2-2015, Tikanga A |
Mooney Liscicoty, ML (1 + 4) 100 ° C | 75 ~ 85 | 75 ~ 85 | 81 | GB / T 15340-2008 Over Te tikanga o te GB / T1232.1 |
300% ahorangi modullus (145 ℃, 50intin Momo 1 tauira 1, tere 500mm / min), MPA | 10.4 ~ 14.4 | 10.1 ~ 14.7 | 13.4 | GB / T 34685-2017 Astm Irb no 8 karamu pango GB / t 528-2009 Patohia te tapahi i ahau |
Te kaha o te kaha (145 ° C, 505min Momo Tauira, Tere 500mm / min), MPA | ≥26.4 | ≥25.3 | 28.9 | |
Elngosation i te wa pakaru (145 ° C, 50min Momo i te tauira, tere 500mm / min),% | ≥490 | ≥460 | 546 | |
|
|
|
|
|
|