| Features | Calor resistentia, canus resistentia et gerunt resistentia |
| Applicatio | familia necessitatibus, Medical Care |
Item | Index | Test modus | Res | Conclusio | |
Superior productio | Qualified uber | ||||
Species | Non-polluat obstructionum lucis coloris gluten, liberi de cocking particulas, harenae et mechanica impudicitiis. | Visus | Normalis | Superior | |
Volatile (%) ≤ | 0.60 | 0.90 | GB / T 24131.1- MMXVIII, calidum volumine Ratio B2 | 0.16 | Superior |
Organicum acidum (%) | 4.50 ~ 6.75 | GB / T 8657- MMXIV, B ratio | 6.16 | Superior | |
Soap content (%) ≤ | 0.40 | 0.04 | Superior | ||
Tenetur styrene (%) | 22.5 ~ 24.5 | GB / T 8658-1998 | 23.7 | Superior | |
Rudis rubber Moneoney Viscosity , Ml (I + IV) C ℃ | XLV ~ LV | XLIV ~ LVI | GB / T 1232.1- MMXVI, super Roll Methodo | L ~ LI | Superior |
Monone Viscositas compositis: Ml (I + IV) C ℃ ≤ | 93 | GB / T 1232.1- MMXVI (ASTM IRB No.8) | 71 | Superior | |
CCC% accentus ad modulus (CXLV ℃, 35min) (MPA) | 16.6 ~ 20.6 | 16,1 ~ 21,1 | GB / T 8656-2018 A (ASTM IRB No.8): GB / T 528-2009 (I Conscidisti cultro) | 18.0 | Superior |
Tensile viribus (CXLV ℃, 35min) (MPa) ≥ | 24.5 | 23.5 | 25.8 | Superior | |
Elongatio ad confractus (CXLV ℃, 35min) (%) ≥ | 350 | 340 | 401 | Superior | |
|
|
|
 |  |  |
| Features | Calor resistentia, canus resistentia et gerunt resistentia |
| Applicatio | familia necessitatibus, Medical Care |
Item | Index | Test modus | Res | Conclusio | |
Superior productio | Qualified uber | ||||
Species | Non-polluat obstructionum lucis coloris gluten, liberi de cocking particulas, harenae et mechanica impudicitiis. | Visus | Normalis | Superior | |
Volatile (%) ≤ | 0.60 | 0.90 | GB / T 24131.1- MMXVIII, calidum volumine Ratio B2 | 0.16 | Superior |
Organicum acidum (%) | 4.50 ~ 6.75 | GB / T 8657- MMXIV, B ratio | 6.16 | Superior | |
Soap content (%) ≤ | 0.40 | 0.04 | Superior | ||
Tenetur styrene (%) | 22.5 ~ 24.5 | GB / T 8658-1998 | 23.7 | Superior | |
Rudis rubber Moneoney Viscosity , Ml (I + IV) C ℃ | XLV ~ LV | XLIV ~ LVI | GB / T 1232.1- MMXVI, super Roll Methodo | L ~ LI | Superior |
Monone Viscositas compositis: Ml (I + IV) C ℃ ≤ | 93 | GB / T 1232.1- MMXVI (ASTM IRB No.8) | 71 | Superior | |
CCC% accentus ad modulus (CXLV ℃, 35min) (MPA) | 16,6 ~ 20.6 | 16,1 ~ 21,1 | GB / T 8656-2018 A (ASTM IRB No.8): GB / T 528-2009 (I Conscidisti cultro) | 18.0 | Superior |
Tensile viribus (CXLV ℃, 35min) (MPa) ≥ | 24.5 | 23.5 | 25.8 | Superior | |
Elongatio ad confractus (CXLV ℃, 35min) (%) ≥ | 350 | 340 | 401 | Superior | |
|
|
|
| | |