| Features | high strength and transparency |
| Application | agricultural film, stretch winding and film winding film |
Analysis Item | Quality Index | Test result | Test method |
Color particles,pcs/kg | ≤10 | 1 | SH/T1541-2006 |
large and small granular,g/kg | ≤10 | 0 | SH/T1541-2006 |
Meltmassflowrate(2.16kg),g/10min | 0.8-1.2 | 1 | GB/T 3682-2000 |
Density(23℃) ，g/cm^3 | 0.918-0.9220 | 0.9203 | GB/T 1033.2-2010 |
Tensile yield stress,MPa | ≥8.5 | 11 | GB/T 1040.2-2006 |
Tensile fracture stress,MPa | ≥23 | 29.6 | GB/T 1040.2-2006 |
Tensile strainat break,% | ≥850 | 1005 | GB/T 1040.2-2006 |
Fisheye 0.8mm pc/1520cm^2 | ≤8 | 1 | GB/T 11115-2009 |
| Fisheye 0.4mm pc/1520cm^2 | ≤20 | 8 | GB/T 11115-2009 |
| Haze % | Measured | 16.6 | GB/T 2410-2008 |
| Impact damage quality | ≥55 | 116 | GB/T 9639.1-2008 |
| Openness | Easy to uncover | Easy to uncover |
 |  |  |  |
 |  |  |
| Features | high strength and transparency |
| Application | agricultural film, stretch winding and film winding film |
Analysis Item | Quality Index | Test result | Test method |
Color particles,pcs/kg | ≤10 | 1 | SH/T1541-2006 |
large and small granular,g/kg | ≤10 | 0 | SH/T1541-2006 |
Meltmassflowrate(2.16kg),g/10min | 0.8-1.2 | 1 | GB/T 3682-2000 |
Density(23℃) ，g/cm^3 | 0.918-0.9220 | 0.9203 | GB/T 1033.2-2010 |
Tensile yield stress,MPa | ≥8.5 | 11 | GB/T 1040.2-2006 |
Tensile fracture stress,MPa | ≥23 | 29.6 | GB/T 1040.2-2006 |
Tensile strainat break,% | ≥850 | 1005 | GB/T 1040.2-2006 |
Fisheye 0.8mm pc/1520cm^2 | ≤8 | 1 | GB/T 11115-2009 |
| Fisheye 0.4mm pc/1520cm^2 | ≤20 | 8 | GB/T 11115-2009 |
| Haze % | Measured | 16.6 | GB/T 2410-2008 |
| Impact damage quality | ≥55 | 116 | GB/T 9639.1-2008 |
| Openness | Easy to uncover | Easy to uncover |
| | | |
| | |