| Features | high rigidity and high flow |
| Application | container |
| Typical Properties | Nominal | ||
Value | Units | Test Method | |
| Physical | |||
Melt Flow Rate, (230 °C/2.16 kg) | 12 | g/10 min | ISO 1133-1 |
Density | 0.90 | g/cm^3 | ISO 1183-1 |
Mechanical | |||
Tensile Modulus | 1400 | MPa | ISO 527-1, -2 |
Tensile Stress at Yield | 35 | MPa | ISO 527-1, -2 |
Tensile Strain at Break | > 50 | % | ISO 527-1, -2 |
| Tensile Strain at Yield | 10 | % | ISO 527-1, -2 |
| Impact | |||
| Charpy Impact Strength - Notched, (23 °C, Type 1, Edgewise, Notch A) | 4 | kJ/m^2 | ISO 179 |
| Thermal | |||
| Vicat Softening Temperature | |||
(A/50 N) (B50) | 153 85 | °C °C | ISO 306 ISO 306 |
| Heat Deflection Temperature B, (0.45 MPa, Unannealed) | 95 | °C | ISO 75B-1, -2 |
|
|
|
 |  |  |
| Features | high rigidity and high flow |
| Application | container |
| Typical Properties | Nominal | ||
Value | Units | Test Method | |
| Physical | |||
Melt Flow Rate, (230 °C/2.16 kg) | 12 | g/10 min | ISO 1133-1 |
Density | 0.90 | g/cm^3 | ISO 1183-1 |
Mechanical | |||
Tensile Modulus | 1400 | MPa | ISO 527-1, -2 |
Tensile Stress at Yield | 35 | MPa | ISO 527-1, -2 |
Tensile Strain at Break | > 50 | % | ISO 527-1, -2 |
| Tensile Strain at Yield | 10 | % | ISO 527-1, -2 |
| Impact | |||
| Charpy Impact Strength - Notched, (23 °C, Type 1, Edgewise, Notch A) | 4 | kJ/m^2 | ISO 179 |
| Thermal | |||
| Vicat Softening Temperature | |||
(A/50 N) (B50) | 153 85 | °C °C | ISO 306 ISO 306 |
| Heat Deflection Temperature B, (0.45 MPa, Unannealed) | 95 | °C | ISO 75B-1, -2 |
|
|
|
| | |