| Vipengee | Ugumu wa juu na mtiririko wa juu |
| Maombi | chombo |
| Mali ya kawaida | Nominal | ||
Thamani | Vitengo | Njia ya mtihani | |
| Mwili | |||
Kiwango cha mtiririko wa kuyeyuka, (230 ° C/2.16 kg) | 12 | g/10 min | ISO 1133-1 |
Wiani | 0.90 | g/cm^3 | ISO 1183-1 |
Mitambo | |||
Modulus tensile | 1400 | MPA | ISO 527-1, -2 |
Dhiki ya tensile katika mavuno | 35 | MPA | ISO 527-1, -2 |
Shina tensile wakati wa mapumziko | > 50 | % | ISO 527-1, -2 |
| Shina tensile katika mavuno | 10 | % | ISO 527-1, -2 |
| Athari | |||
| Nguvu ya Athari ya Charpy - iliyowekwa, (23 ° C, Aina 1, Edgewise, Notch A) | 4 | KJ/M^2 | ISO 179 |
| Mafuta | |||
| Joto la kunyoa la Vicat | |||
(A/50 N) (B50) | 153 85 | ° C. ° C. | ISO 306 ISO 306 |
| Joto la kupunguka kwa joto B, (0.45 MPa, halijafungwa) | 95 | ° C. | ISO 75B -1, -2 |
|
|
|
 |  |  |
| Vipengee | Ugumu wa juu na mtiririko wa juu |
| Maombi | chombo |
| Mali ya kawaida | Nominal | ||
Thamani | Vitengo | Njia ya mtihani | |
| Mwili | |||
Kiwango cha mtiririko wa kuyeyuka, (230 ° C/2.16 kg) | 12 | g/10 min | ISO 1133-1 |
Wiani | 0.90 | g/cm^3 | ISO 1183-1 |
Mitambo | |||
Modulus tensile | 1400 | MPA | ISO 527-1, -2 |
Dhiki ya tensile katika mavuno | 35 | MPA | ISO 527-1, -2 |
Shina tensile wakati wa mapumziko | > 50 | % | ISO 527-1, -2 |
| Shina tensile katika mavuno | 10 | % | ISO 527-1, -2 |
| Athari | |||
| Nguvu ya Athari ya Charpy - iliyowekwa, (23 ° C, Aina 1, Edgewise, Notch A) | 4 | KJ/M^2 | ISO 179 |
| Mafuta | |||
| Joto la kunyoa la Vicat | |||
(A/50 N) (B50) | 153 85 | ° C. ° C. | ISO 306 ISO 306 |
| Joto la kupunguka kwa joto B, (0.45 MPa, halijafungwa) | 95 | ° C. | ISO 75B -1, -2 |
|
|
|
| | |