| Features | Maximum rigiditatem et altum fluxus |
| Applicatio | continens |
| Typical proprietatibus | Nominal | ||
Valor | Unitates | Test modus | |
| Physica | |||
Rate conflandum fluxus (CCXXX ° C / 2.16 kg) | 12 | G / X min | ISO 1133-1 |
Densitas | 0.90 | G / III cm ^ | ISO 1183-1 |
Mechanica | |||
Tensile modulus | 1400 | MPA | ISO 527-1, -2 |
Tensile accentus ad cede | 35 | MPA | ISO 527-1, -2 |
Tensile iactabantur ad confractus | > L | % | ISO 527-1, -2 |
| Tensile iactabantur ad cede | 10 | % | ISO 527-1, -2 |
| Impulsus | |||
| Charypy Impact fortitudinem - Notched (XXIII ° C, Type I, EdgeWish, SCARIFATIO a) | 4 | KJ / m ^ II | ISO CLXXIX |
| Scelerum | |||
| Vicat mollitorum temperatus | |||
(A / L N) (B50) | 153 85 | N ° C N ° C | ISO CCCVI ISO CCCVI |
| Calor Deflection Temperature B (0.45 MPA, unannnealed) | 95 | N ° C | ISO 75b-I, -2 |
|
|
|
 |  |  |
| Features | Maximum rigiditatem et altum fluxus |
| Applicatio | continens |
| Typical proprietatibus | Nominal | ||
Valor | Unitates | Test modus | |
| Physica | |||
Rate conflandum fluxus (CCXXX ° C / 2.16 kg) | 12 | G / X min | ISO 1133-1 |
Densitas | 0.90 | G / III cm ^ | ISO 1183-1 |
Mechanica | |||
Tensile modulus | 1400 | MPA | ISO 527-1, -2 |
Tensile accentus ad cede | 35 | MPA | ISO 527-1, -2 |
Tensile iactabantur ad confractus | > L | % | ISO 527-1, -2 |
| Tensile iactabantur ad cede | 10 | % | ISO 527-1, -2 |
| Impulsus | |||
| Charypy Impact fortitudinem - Notched (XXIII ° C, Type I, EdgeWish, SCARIFATIO a) | 4 | KJ / m ^ II | ISO CLXXIX |
| Scelerum | |||
| Vicat mollitorum temperatus | |||
(A / L N) (B50) | 153 85 | N ° C N ° C | ISO CCCVI ISO CCCVI |
| Calor Deflection Temperature B (0.45 MPA, unannnealed) | 95 | N ° C | ISO 75b-I, -2 |
|
|
|
| | |