| Features | heat sealing, high impact resistance, high strength, stress cracking resistance and transparency |
| Application | film, packaging |
Item | Quality Index | Test result | Experiment method |
| Granular appearance Colored Granular pc/kg Large and small granular g/kg | ≤5 ≤10 | 0 0.1 | SH/T 1541-2006 |
Melt mass flow rate g/10min | 7.0～9.0 | 7.3 | GB/T 3682-2000 |
Tensile yield stress MPa | Measurement | 23.8 | GB/T 1040.2-2006 |
Izod impact strength (23) J/m | Measurement | 36 | GB/T 1843-2008 |
Flexural modulus MPa | Measurement | 786 | GB/T 9341-2008 |
Fisheye 0.4mm/1520cmü | ≤20 | 8 | GB/T 6595-1986 |
Fisheye 0.8mm/1520cmü | ≤5 | 1 | GB/T 6595-1986 |
 |  |  |  |
 |  |  |
| Features | heat sealing, high impact resistance, high strength, stress cracking resistance and transparency |
| Application | film, packaging |
Item | Quality Index | Test result | Experiment method |
| Granular appearance Colored Granular pc/kg Large and small granular g/kg | ≤5 ≤10 | 0 0.1 | SH/T 1541-2006 |
Melt mass flow rate g/10min | 7.0～9.0 | 7.3 | GB/T 3682-2000 |
Tensile yield stress MPa | Measurement | 23.8 | GB/T 1040.2-2006 |
Izod impact strength (23) J/m | Measurement | 36 | GB/T 1843-2008 |
Flexural modulus MPa | Measurement | 786 | GB/T 9341-2008 |
Fisheye 0.4mm/1520cmü | ≤20 | 8 | GB/T 6595-1986 |
Fisheye 0.8mm/1520cmü | ≤5 | 1 | GB/T 6595-1986 |
| | | |
| | |