Features | high toughness, aging resistance |
Application | containers, agricultural films, shrink films, packaging, plastic bags |
Analysis Item | Excellent Product | Qualified Product | Test result | Experiment method |
Black Particles | 0 | 0 | 0 | SH/T 1541-2006 |
Color Particles | ≤10 | ≤6 | 0 | SH/T 1541-2006 |
Large and Small Particle,g/kg | report | report | 0 | SH/T 1541-2006 |
Tail Particles | ≤20 | ≤40 | 0 | SH/T 1541-2006 |
Floc,g/kg | report | report | 0 | SH/T 1541-2006 |
Density,g/cm^3 | 0.9225±0.0020 | 0.9225±0.0030 | 0.9213 | GB/T 1033.2-2010 |
MFR,g/10min | 2.0±0.2 | 2.0±0.3 | 2 | GB/T 3682-2000 |
Nominal Tensile Strain at Break,% | ≥70 | ≥70 | 110 | GB/T 1040.2-2006 |
Tensile Strength at Break,Mpa | ≥11 | ≥9.5 | 11.5 | GB/T 1040.2-2006 |
Haze,% | ≤9.0 | ≤9.0 | 7.7 | GB/T 2410-2008 |
Fish- eyes,0.3mm-2.0mm /1200cm^2 | ≤15 | ≤30 | 11 | GB/T 11115-2009 |
Stripe | ≤20 | ≤20 | 0 | GB/T 11115-2009 |
Features | high toughness, aging resistance |
Application | containers, agricultural films, shrink films, packaging, plastic bags |
Analysis Item | Excellent Product | Qualified Product | Test result | Experiment method |
Black Particles | 0 | 0 | 0 | SH/T 1541-2006 |
Color Particles | ≤10 | ≤6 | 0 | SH/T 1541-2006 |
Large and Small Particle,g/kg | report | report | 0 | SH/T 1541-2006 |
Tail Particles | ≤20 | ≤40 | 0 | SH/T 1541-2006 |
Floc,g/kg | report | report | 0 | SH/T 1541-2006 |
Density,g/cm^3 | 0.9225±0.0020 | 0.9225±0.0030 | 0.9213 | GB/T 1033.2-2010 |
MFR,g/10min | 2.0±0.2 | 2.0±0.3 | 2 | GB/T 3682-2000 |
Nominal Tensile Strain at Break,% | ≥70 | ≥70 | 110 | GB/T 1040.2-2006 |
Tensile Strength at Break,Mpa | ≥11 | ≥9.5 | 11.5 | GB/T 1040.2-2006 |
Haze,% | ≤9.0 | ≤9.0 | 7.7 | GB/T 2410-2008 |
Fish- eyes,0.3mm-2.0mm /1200cm^2 | ≤15 | ≤30 | 11 | GB/T 11115-2009 |
Stripe | ≤20 | ≤20 | 0 | GB/T 11115-2009 |