Maombi | Vyombo, chupa za plastiki |
Mradi |
Sehemu |
Kielelezo cha Ufundi |
Matokeo |
Njia ya majaribio |
|
Muonekano wa granular |
Nafaka za rangi nyeusi za Spotand |
PC/kg |
≤6 |
2 |
SH/T 1541.1 |
Kuyeyuka kiwango cha mtiririko wa molekuli |
190 ℃, 21.6kg |
g/10min |
28 ~ 38 |
31.6 |
GB/T 3682.1 |
Wiani |
g/cm3 |
0.951 ~ 0.955 |
0.9545 |
GB/T 1033.2 |
|
Mafadhaiko ya mavuno ya tensile |
MPA |
≥23 |
26.6 |
GB/T 1040.2 |
|
Kuvunja kwa nguvu ya kawaida |
% |
≥150 |
211 |
||
Charpy notched athari ya athari |
KJ/M^2 |
≥7 |
10 |
GB/T 1043.1 |
|
Modulus ya kubadilika |
MPA |
≥700 |
1120 |
GB/T 9341 |
![]() |
![]() |
![]() |
![]() |
![]() |
Maombi | Vyombo, chupa za plastiki |
Mradi |
Sehemu |
Kielelezo cha Ufundi |
Matokeo |
Njia ya majaribio |
|
Muonekano wa granular |
Nafaka za rangi nyeusi za Spotand |
PC/kg |
≤6 |
2 |
SH/T 1541.1 |
Kuyeyuka kiwango cha mtiririko wa molekuli |
190 ℃, 21.6kg |
g/10min |
28 ~ 38 |
31.6 |
GB/T 3682.1 |
Wiani |
g/cm3 |
0.951 ~ 0.955 |
0.9545 |
GB/T 1033.2 |
|
Mafadhaiko ya mavuno ya tensile |
MPA |
≥23 |
26.6 |
GB/T 1040.2 |
|
Kuvunja kwa nguvu ya kawaida |
% |
≥150 |
211 |
||
Charpy notched athari ya athari |
KJ/M^2 |
≥7 |
10 |
GB/T 1043.1 |
|
Modulus ya kubadilika |
MPA |
≥700 |
1120 |
GB/T 9341 |
![]() |
![]() |
![]() |
![]() |
![]() |