| Features | high gloss and high rigidity |
| Application | Thin-walled packaging, containers, non-woven fabrics and fibers |
Analysis Project | Unit | Technical indicators | Test result | Test method | |
Granular Appearance | Color granular | pc/kg | ≤30 | 0 | SH/T1541.1-2019 |
Large and small granular | g/kg | 0 | 0 | ||
Isotactic index | % | 96.5±2.0 | 98.3 | GB/T2412-2008 | |
Melt mass flow rate (MFR) 190°C, 2. 16kg | g/10min | 26+3 | 25.7 | GB/T3682.1-2018 | |
Tensile Yield Stress (oy) | Mpa | ≥29 | 31.8 | GB/T1040.2-2022 | |
Tensile Nominal Strain at Break (gtB) | % | ≥300 | 632 | ||
Tensile elastic modulus (Et) | Mpa | Report | 1013 | ||
Tensile breaking stress (σ B) | Mpa | >8.0 | 19.5 | ||
 |  |  |  |
 |  |  |
| Features | high gloss and high rigidity |
| Application | Thin-walled packaging, containers, non-woven fabrics and fibers |
Analysis Project | Unit | Technical indicators | Test result | Test method | |
Granular Appearance | Color granular | pc/kg | ≤30 | 0 | SH/T1541.1-2019 |
Large and small granular | g/kg | 0 | 0 | ||
Isotactic index | % | 96.5±2.0 | 98.3 | GB/T2412-2008 | |
Melt mass flow rate (MFR) 190°C, 2. 16kg | g/10min | 26+3 | 25.7 | GB/T3682.1-2018 | |
Tensile Yield Stress (oy) | Mpa | ≥29 | 31.8 | GB/T1040.2-2022 | |
Tensile Nominal Strain at Break (gtB) | % | ≥300 | 632 | ||
Tensile elastic modulus (Et) | Mpa | Report | 1013 | ||
Tensile breaking stress (σ B) | Mpa | >8.0 | 19.5 | ||
| | | |
| | |