| Maombi | Tubing |
Bidhaa ya mtihani, kitengo | Bidhaa bora | Matokeo ya mtihani | |
Mnato ml/g | 127-135 | 133 | |
Wiani dhahiri g/ml | ≥ | 0.45 | 0.50 |
Jambo tete (pamoja na maji) sehemu ya molekuli % | ≤ | 0.30 | 0.28 |
Mabaki ya ungo 250μn, shimo la ungo % % | ≤ | 1.6 | 1.5 |
Mabaki ya ungo 63μn, shimo la ungo % % | ≥ | 97 | 99 |
Fisheye pc/400cm^2 | ≤ | 20 | 17 |
100g resin plastikiezer kunyonya, g | ≥ | 26 | - |
Weupe (160 ℃, 10min) % | ≥ | 78 | 84 |
| Uchafu, PC | ≤ | 16 | 16 |
| Yaliyomo ya polyethilini ya monomer, μg/g | ≤ | 5.0 | 2 |
| Utaratibu wa benzini ya maji, μs/(cm*g) | ≤ | 5.0 | 2 |
|
|
|
 |  |  |
| Maombi | Tubing |
Bidhaa ya mtihani, kitengo | Bidhaa bora | Matokeo ya mtihani | |
Mnato ml/g | 127-135 | 133 | |
Wiani dhahiri g/ml | ≥ | 0.45 | 0.50 |
Jambo tete (pamoja na maji) sehemu ya molekuli % | ≤ | 0.30 | 0.28 |
Mabaki ya ungo 250μn, shimo la ungo % % | ≤ | 1.6 | 1.5 |
Mabaki ya ungo 63μn, shimo la ungo % % | ≥ | 97 | 99 |
Fisheye pc/400cm^2 | ≤ | 20 | 17 |
100g resin plastikiezer kunyonya, g | ≥ | 26 | - |
Weupe (160 ℃, 10min) % | ≥ | 78 | 84 |
| Uchafu, PC | ≤ | 16 | 16 |
| Yaliyomo ya polyethilini ya monomer, μg/g | ≤ | 5.0 | 2 |
| Utaratibu wa benzini ya maji, μs/(cm*g) | ≤ | 5.0 | 2 |
|
|
|
| | |