Features | high strength, aging resistance |
Application | pipes, hot water pipes |
Analysis Project | Quality Index | Test result | Test Method | |
Granule appearance (color granule), pcs/kg | ≤10 | 0 | SH/T 1541.1-2019 | |
Melt mass flow rate (2.16kg), g/10min | 0.20-0.30 | 0.24 | GB/T 3682.1-2018 | |
Tensile yield stress,MPa | ≥20.0 | 23.0 | GB/T 1040.2-2006 | |
Tensile breaking stress,% | ≥300 | 566 | GB/T 1040.2-2006 | |
Charpy impact strength, kJ/m^2 | ≥40 | 45 | GB/T 1043.1-2008 | |
Flexural modulus, MPa | ≥620 | 664 | GB/T 9341-2008 | |
Heat distortion temperature 0.45Mpa, ℃ | Report | 61 | GB/T 1634.2-2019 |
Features | high strength, aging resistance |
Application | pipes, hot water pipes |
Analysis Project | Quality Index | Test result | Test Method | |
Granule appearance (color granule), pcs/kg | ≤10 | 0 | SH/T 1541.1-2019 | |
Melt mass flow rate (2.16kg), g/10min | 0.20-0.30 | 0.24 | GB/T 3682.1-2018 | |
Tensile yield stress,MPa | ≥20.0 | 23.0 | GB/T 1040.2-2006 | |
Tensile breaking stress,% | ≥300 | 566 | GB/T 1040.2-2006 | |
Charpy impact strength, kJ/m^2 | ≥40 | 45 | GB/T 1043.1-2008 | |
Flexural modulus, MPa | ≥620 | 664 | GB/T 9341-2008 | |
Heat distortion temperature 0.45Mpa, ℃ | Report | 61 | GB/T 1634.2-2019 |