| Application | Medical infusion bottle |
Analysis Item |
Quality Index |
Test result |
Test method |
Melt mass flow rate, g/10min |
2.1-2.5 |
2.39 |
GB/T3682.1-2018 |
Tensile fracture stress,Mpa |
≥11 |
11.3 |
GB/T1040 |
Tensile fracture strain,% |
≥80 |
103 |
GB/T1040 |
Dielectric constant（1MHz） |
≤2.3 |
2.22 |
GB/T 1409 |
Vica softening temperature,°C |
≥85 |
91.3 |
Load 10N, heating rate 50°C/H |
Density,g/cm^3 |
0.9180-0.9220 |
0.9211 |
GB/T 1033.2 |
|
 |
 |
|
 |
 |
 |
| Application | Medical infusion bottle |
Analysis Item |
Quality Index |
Test result |
Test method |
Melt mass flow rate, g/10min |
2.1-2.5 |
2.39 |
GB/T3682.1-2018 |
Tensile fracture stress,Mpa |
≥11 |
11.3 |
GB/T1040 |
Tensile fracture strain,% |
≥80 |
103 |
GB/T1040 |
Dielectric constant（1MHz） |
≤2.3 |
2.22 |
GB/T 1409 |
Vica softening temperature,°C |
≥85 |
91.3 |
Load 10N, heating rate 50°C/H |
Density,g/cm^3 |
0.9180-0.9220 |
0.9211 |
GB/T 1033.2 |
|
|
|
|
|
|
|