| Kiasi: | |
|---|---|
| Vipengee | Nguvu ya juu |
| Maombi | Filamu ya ufungaji |
Bidhaa | Faharisi ya ubora | Matokeo ya mtihani | Njia ya mtihani |
Kuonekana kuwa kubwa na ndogo, granular, pc/kg | Ripoti | 1 | SH/T 1541.1 |
Kuonekana ngozi ya ngozi na granular ya granular, PC/kg | Ripoti | 5 | SH/T 1541.1 |
Kuonekana nyeusi granular, pc/kg | ≤10 | 5 | SH/T 1541.1 |
Kiwango cha mtiririko wa misa, g/10min | 0.70 ~ 1.30 | 0.94 | GB/T 3682.1-2018 190 ℃/2.16kg |
Wiani (23 ℃), g/cm^3 | 0.9160 ~ 0.9220 | 0.9202 | GB/T 1033.2 |
Dhiki ya mavuno ya tensile, MPA | ≥7.0 | 11.3 | GB/T 1040.2 |
Tensile Fracture ya kawaida,% | ≥300 | 705 | GB/T 1040.2 |
Macho ya samaki 0.4mm, pc/1520cm^2 | ≤40 | 2 | GB/T 11115-2009 |
Macho ya samaki0.8mm, pc/1520cm^2 | ≤8 | 0 | GB/T 11115-2009 |
Uharibifu mkubwa unaosababishwa na kuanguka kwa athari ya dart (unene wa filamu 0.030mm), g | Ripoti | 956 | GB/T 9639.1-2008 |
 |  |  |  |
 |  |  |
| Vipengee | Nguvu ya juu |
| Maombi | Filamu ya ufungaji |
Bidhaa | Faharisi ya ubora | Matokeo ya mtihani | Njia ya mtihani |
Kuonekana kuwa kubwa na ndogo, granular, pc/kg | Ripoti | 1 | SH/T 1541.1 |
Kuonekana ngozi ya ngozi na granular ya granular, PC/kg | Ripoti | 5 | SH/T 1541.1 |
Kuonekana nyeusi granular, pc/kg | ≤10 | 5 | SH/T 1541.1 |
Kiwango cha mtiririko wa misa, g/10min | 0.70 ~ 1.30 | 0.94 | GB/T 3682.1-2018 190 ℃/2.16kg |
Wiani (23 ℃), g/cm^3 | 0.9160 ~ 0.9220 | 0.9202 | GB/T 1033.2 |
Dhiki ya mavuno ya tensile, MPA | ≥7.0 | 11.3 | GB/T 1040.2 |
Tensile Fracture ya kawaida,% | ≥300 | 705 | GB/T 1040.2 |
Macho ya samaki 0.4mm, pc/1520cm^2 | ≤40 | 2 | GB/T 11115-2009 |
Macho ya samaki0.8mm, pc/1520cm^2 | ≤8 | 0 | GB/T 11115-2009 |
Uharibifu mkubwa unaosababishwa na kuanguka kwa athari ya dart (unene wa filamu 0.030mm), g | Ripoti | 956 | GB/T 9639.1-2008 |
| | | |
| | |