| Applicatio | Tubing |
Item | Superior | Primo gradu | Qualified uber | TRIEN | |
Mediocris gradu polymerization | 1135-981 | 1060 | |||
Numerus inmunditia | ≤ | 16 | 30 | 60 | 4 |
Volatile (including aqua) contentus (%) | ≤ | 0.3 | 0.3 | 0.5 | 0.131 |
Apparens Density (G / ML) | Tago | 0.48 | 0.48 | 0.45 | 0.535 |
Sieve residue% | CCL μm mesh ≤ | 1.6 | 2 | 8 | 0.04 |
LXIII μm mesh ≥ | 97 | 90 | 85 | 99.16 | |
Piscium oculi numero (6min152 ℃) / 400cm ^ II | ≤ | 20 | 30 | 60 | 15 |
100g resin plasticizer effusio (G) | Tago | 21 | 19 | - | 25 |
White (CLX ℃, 10min) /% | Tago | 80 | 78 | 70 | 84 |
RELICTUM Vinyl chloride content (UG / G) | ≤ | 3 | 5 | 10 | 0.1 |
|
|
|
 |  |  |
| Applicatio | Tubing |
Item | Superior | Primo gradu | Qualified uber | TRIEN | |
Mediocris gradu polymerization | 1135-981 | 1060 | |||
Numerus inmunditia | ≤ | 16 | 30 | 60 | 4 |
Volatile (including aqua) content (%) | ≤ | 0.3 | 0.3 | 0.5 | 0.131 |
Apparent Density (G / ML) | Tago | 0.48 | 0.48 | 0.45 | 0.535 |
Sieve residue% | CCL μm mesh ≤ | 1.6 | 2 | 8 | 0.04 |
LXIII μm mesh ≥ | 97 | 90 | 85 | 99.16 | |
Piscium oculi numero (6min152 ℃) / 400cm ^ II | ≤ | 20 | 30 | 60 | 15 |
100g resin plasticizer effusio (G) | Tago | 21 | 19 | - | 25 |
White (CLX ℃, 10min) /% | Tago | 80 | 78 | 70 | 84 |
RELICTUM Vinyl chloride content (UG / G) | ≤ | 3 | 5 | 10 | 0.1 |
|
|
|
| | |