| Applicatio | Termario CPP calor signantes layer, quibus ostium agente et lapsus agente |
Item |
Index |
TRIEN |
Experimentum modum |
| CALLA Coloratus Granular PC / kg Magna et parva granuloso g / kg |
≤5 ≤10 |
0 0.2 |
Sh / T 1541-2006 |
Meltere massa fluxus rate g / 10min |
6.0 ~ 9,0 |
7.2 |
GB / T 3682-2000 |
Tensile cede accentus MPA |
≥18.0 |
21 |
GB / T 1040.2-2006 |
Flexural modulum, MPA |
≥55050 |
627 |
GB / T 9341-2008 |
XXIII Prophetia Ruth Africa, KJ / Mu |
≥5.0 |
5.4 |
GB / T 1043.1-2008 |
Vicat softening punctum, A120, ℃ |
≤118 |
115 |
GB / T 1633-2000 |
Index |
≤2.0 |
-6.4 |
HG / T 3862-2006 |
 |
 |
 |
 |
 |
 |
 |
| Applicatio | Termario CPP calor signantes layer, quibus ostium agente et lapsus agente |
Item |
Index |
TRIEN |
Experimentum modum |
| CALLA Coloratus Granular PC / kg Magna et parva granuloso g / kg |
≤5 ≤10 |
0 0.2 |
Sh / T 1541-2006 |
Meltere massa fluxus rate g / 10min |
6.0 ~ 9,0 |
7.2 |
GB / T 3682-2000 |
Tensile cede accentus MPA |
≥18.0 |
21 |
GB / T 1040.2-2006 |
Flexural modulum, MPA |
≥55050 |
627 |
GB / T 9341-2008 |
XXIII Prophetia Ruth Africa, KJ / Mu |
≥5.0 |
5.4 |
GB / T 1043.1-2008 |
Vicat softening punctum, A120, ℃ |
≤118 |
115 |
GB / T 1633-2000 |
Index |
≤2.0 |
-6.4 |
HG / T 3862-2006 |
|
|
|
|
|
|
|