| Vipengee | Ugumu mkubwa, upanuzi, upinzani wa oksidi na ugumu wa hali ya juu |
| Maombi | Ufungaji wa chakula, filamu ya ufungaji, ufungaji, ufungaji laini |
Mradi | Sehemu | Ufundi Kielelezo | Matokeo | Njia ya majaribio | |
Muonekano wa granular | Nafaka za rangi nyeusi za Spotand | PC/kg | ≤15 | 2 | SH/T 1541.1 |
Nyoka na mikia | PC/kg | ≤15 | 1 | ||
Kubwa na ndogo | g/kg | ≤10 | 0 | ||
Kuyeyuka kwa mtiririko wa molekuli | 190 ℃, 5.0kg | g/10min | 0.30 ~ 0.43 | 0.4 | GB/T 3682.1 |
Wiani | g/cm^2 | 0.955 ~ 0.959 | 0.9578 | GB/T 1033.2 | |
Mafadhaiko ya mavuno ya tensile | MPA | ≥7.0 | 27.9 | GB/T 1040.2 | |
Tensile nominenal shida wakati wa mapumziko | % | ≥90 | 722 | GB/T 1040.2 | |
Fisheye | 0.8mm | PC/1520cm^2 | ≤8 | 1 | GB/T 11115 |
0.4mm | PC/1520cm^2 | ≤40 | 1 | ||
Nguvu ya athari ya DART | g | Kipimo | 83 | GB/T 9639.1 | |
 |  |  |  |
 |  |  |
| Vipengee | Ugumu mkubwa, upanuzi, upinzani wa oksidi na ugumu wa hali ya juu |
| Maombi | Ufungaji wa chakula, filamu ya ufungaji, ufungaji, ufungaji laini |
Mradi | Sehemu | Ufundi Kielelezo | Matokeo | Njia ya majaribio | |
Muonekano wa granular | Nafaka za rangi nyeusi za Spotand | PC/kg | ≤15 | 2 | SH/T 1541.1 |
Nyoka na mikia | PC/kg | ≤15 | 1 | ||
Kubwa na ndogo | g/kg | ≤10 | 0 | ||
Kuyeyuka kwa mtiririko wa molekuli | 190 ℃, 5.0kg | g/10min | 0.30 ~ 0.43 | 0.4 | GB/T 3682.1 |
Wiani | g/cm^2 | 0.955 ~ 0.959 | 0.9578 | GB/T 1033.2 | |
Mafadhaiko ya mavuno ya tensile | MPA | ≥7.0 | 27.9 | GB/T 1040.2 | |
Tensile nominenal shida wakati wa mapumziko | % | ≥90 | 722 | GB/T 1040.2 | |
Fisheye | 0.8mm | PC/1520cm^2 | ≤8 | 1 | GB/T 11115 |
0.4mm | PC/1520cm^2 | ≤40 | 1 | ||
Nguvu ya athari ya DART | g | Kipimo | 83 | GB/T 9639.1 | |
| | | |
| | |